Dimension
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanical
Property | Value | Comment |
---|---|---|
Elongation | 13 % Show Supplier Material materials with Elongation of 13 % | min. | for thickness 0.45-0.5 mm | A80 |
15 % Show Supplier Material materials with Elongation of 15 % | min. | for thickness 0.5-0.7 mm | A80 | |
17 % Show Supplier Material materials with Elongation of 17 % | min. | for thickness 0.7-6 mm | A80 | |
Tensile strength | 390 MPa Show Supplier Material materials with Tensile strength of 390 MPa | min. | for thickness 0.45-6 mm |
Yield strength | 320 MPa Show Supplier Material materials with Yield strength of 320 MPa | min. | for thickness 0.45-6 mm |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.2 % Show Supplier Material materials with Carbon of 0.2 % | max. |
Manganese | 1.7 % Show Supplier Material materials with Manganese of 1.7 % | max. |
Phosphorus | 0.1 % Show Supplier Material materials with Phosphorus of 0.1 % | max. |
Silicon | 0.6 % Show Supplier Material materials with Silicon of 0.6 % | max. |
Sulfur | 0.045 % Show Supplier Material materials with Sulfur of 0.045 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | Magnelis® can be used in numerous industrial applications, such as: | |
Certifications | Magnelis® is approved for use in Civil Construction by different national bodies: | |
Chemical composition | If, by agreement at the time of enquiry and order, other chemical elements are added, they shall be mentioned on the inspection document which may need a change of classification. | |
Coating | ||
Other | Storage Magnelis® is supplied passivated and/or oiled to temporarily limit any risk of white rust formation. During transport and storage, all necessary precautions must be taken to keep the material dry and to prevent the formation of condensation. | |
Processing methods | The forming techniques currently used for galvanised steel are also suitable for Magnelis®. Magnelis® behaves very well during profiling operations. The coating thickness must be compatible with both the desired degree of corrosion protection and the requirements of the forming processes envisaged. A minimum bending radius of 2x sheet thickness is recommended. | |
Welding | In resistance spot welding, the welding current must be suitably regulated and regularly adjusted. Electrode life can be extended by regularly stepping up the welding current and periodically dressing (machining) the electrodes. The coating thickness must be compatible with both the desired degree of corrosion protection and the requirements of the welding processes envisaged. Magnelis® can be arc welded, laser welded, brazed or high frequency induction welded, taking the same precautions as with galvanised steel. For use in outdoor applications a reprotection of the weld seams from arc welding and high frequency induction welding is recommended. |