Hiperco 50A Bar 69.9 mm

.XLSX
.PDF
Save

Description

An alloy of 49% cobalt, and 2% vanadium, balance iron, Hiperco 50 and Hiperco 50A have the highest magnetic saturation of all soft-magnetic alloys and excel in applications where this attribute is needed. Hiperco 50 maintains its strength after heat treating making it your best choice for applications that experience high forces (e.g. rotating parts).

Primary standard name

Equivalent standard names

Properties

Dimension

Length l

3050 - 3668 mm

Mill random length

Width w

69.9 mm

Electrical

Electrical resistivity ρel

4E-7 Ω·m at 20 °C

General

Density ρ

8.12 g/cm³ at 20 °C

Magnetic

Curie temperature Tc

940 °C at 20 °C

Mechanical

Elastic modulus E

207 GPa at 20 °C

Elongation A

7 % at 20 °C

in 2 in.

Hardness, Rockwell B HRB

20 [-] at 20 °C

Tensile strength Rm

717 MPa at 20 °C

Yield strength YS

365 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

1.04E-5 1/K at 450 °C

Melting point Tm

1427 °C

Specific heat capacity cp

420 J/(kg·K) at 20 °C

Thermal conductivity λ

29 W/(m·K) at 20 °C

Chemical properties

Element

Weight %

Comment

Fe

-

balance

Co

48.75 %

V

2 %

Si

0.05 %

Mn

0.05 %

More

Technological properties

Application areas

A common application of HIPERCO 50A is: Transformer laminations

This material data has been provided by Ed Fagan Inc..

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.