Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.5 GPa Show Supplier Material materials with Elastic modulus of 8.5 GPa | ISO 527-2 (1mm/min) |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ISO 527-2 (5mm/min) |
Flexural modulus | 23.0 °C | 7.4 GPa Show Supplier Material materials with Flexural modulus of 7.4 GPa | ISO 178 (2mm/min) |
Flexural strength | 23.0 °C | 220 MPa Show Supplier Material materials with Flexural strength of 220 MPa | ISO 178 (2mm/min) |
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 65 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A |
Impact strength, Izod unnotched | 23.0 °C | 55 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 55 kJ/m² | ISO 180/1U |
Tensile strength | 23.0 °C | 170 MPa Show Supplier Material materials with Tensile strength of 170 MPa | ISO 527-2 (5mm/min) |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ash content | 23.0 °C | 25 % Show Supplier Material materials with Ash content of 25 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 255 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 255 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75-2/A | |||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 3146 | |||
Flammability | UL94 (0.8mm) HB |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 400 V Show Supplier Material materials with Comparative tracking index of 400 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid 66 GFH compounds are used in all sectors of industry especially automotive under the hood applications, offering an excellent balance of thermal and mechanical properties. Its good for long term heat resistance as well as hyrdolysis resistant applications. | |
Fillers | 25% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |