General
Dimension
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive modulus | 23.0 °C | 127 MPa Show Material materials with Compressive modulus of 127 MPa | ASTM D3039 |
Compressive modulus, transverse | 23.0 °C | 10.2 MPa Show Material materials with Compressive modulus, transverse of 10.2 MPa | ASTM D3039 |
Compressive strength | 23.0 °C | 1365 MPa Show Material materials with Compressive strength of 1365 MPa | ASTM D3039 |
Compressive strength, transverse | 23.0 °C | 196 MPa Show Material materials with Compressive strength, transverse of 196 MPa | ASTM D3039 |
Elastic modulus | 23.0 °C | 137 GPa Show Material materials with Elastic modulus of 137 GPa | ASTM D3039 |
Elastic modulus, transverse | 23.0 °C | 9.2 GPa Show Material materials with Elastic modulus, transverse of 9.2 GPa | ASTM D3039 |
Flexural modulus | 23.0 °C | 132 GPa Show Material materials with Flexural modulus of 132 GPa | ASTM D790 (L/D=32, Vf=61%) |
Flexural modulus, transverse | 23.0 °C | 8.8 GPa Show Material materials with Flexural modulus, transverse of 8.8 GPa | ASTM D790 (L/D=32, Vf=61%) |
Flexural strength | 23.0 °C | 1745 MPa Show Material materials with Flexural strength of 1745 MPa | ASTM D790 (L/D=32, Vf=61%) |
Flexural strength, transverse | 23.0 °C | 102 MPa Show Material materials with Flexural strength, transverse of 102 MPa | ASTM D790 (L/D=32, Vf=61%) |
Interlaminar shear strength | 23.0 °C | 97 MPa Show Material materials with Interlaminar shear strength of 97 MPa | ASTM D2344 (L/D=4, Vf=59%) |
Tensile strength | 23.0 °C | 2572 MPa Show Material materials with Tensile strength of 2572 MPa | ASTM D3039 |
Tensile strength, transverse | 23.0 °C | 81 MPa Show Material materials with Tensile strength, transverse of 81 MPa | ASTM D3039 |
Tow tensile modulus | 23.0 °C | 234 GPa Show Material materials with Tow tensile modulus of 234 GPa | SRM 16 (typical fibre properties) |
Tow tensile strength | 23.0 °C | 4830 MPa Show Material materials with Tow tensile strength of 4830 MPa | SRM 16 (typical fibre properties) |
Technological properties
Property | ||
---|---|---|
Processing history | Epoxy sized 1.2% |