General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2 - 2.2 g/cm³ Show Material materials with Density of 2 - 2.2 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Compressive strength | 23.0 °C | 1100 - 1130 MPa Show Material materials with Compressive strength of 1100 - 1130 MPa |
Elastic modulus | 23.0 °C | 71 - 74 GPa Show Material materials with Elastic modulus of 71 - 74 GPa |
Flexural strength | 23.0 °C | 40 - 100 MPa Show Material materials with Flexural strength of 40 - 100 MPa |
Hardness, Knoop, HK2 | 23.0 °C | 520 - 710 [-] Show Material materials with Hardness, Knoop, HK2 of 520 - 710 [-] |
Hardness, Vickers | 23.0 °C | 900 - 1030 [-] Show Material materials with Hardness, Vickers of 900 - 1030 [-] |
Poisson's ratio | 23.0 °C | 0.16 - 0.17 [-] Show Material materials with Poisson's ratio of 0.16 - 0.17 [-] |
Shear modulus | 23.0 °C | 30 GPa Show Material materials with Shear modulus of 30 GPa |
Tensile strength | 23.0 °C | 50 - 60 MPa Show Material materials with Tensile strength of 50 - 60 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Annealing temperature | 1040 - 1220 °C Show Material materials with Annealing temperature of 1040 - 1220 °C | |
Coefficient of thermal expansion | 600.0 °C | 5.4E-7 - 6.4E-7 1/K Show Material materials with Coefficient of thermal expansion of 5.4E-7 - 6.4E-7 1/K |
Specific heat capacity | 23.0 °C | 670 - 750 J/(kg·K) Show Material materials with Specific heat capacity of 670 - 750 J/(kg·K) |
Thermal conductivity | 23.0 °C | 1.1 - 1.4 W/(m·K) Show Material materials with Thermal conductivity of 1.1 - 1.4 W/(m·K) |
Thermal diffusivity | 23.0 °C | 0.75 - 0.85 mm²/s Show Material materials with Thermal diffusivity of 0.75 - 0.85 mm²/s |
Vicat softening temperature | 1590 - 1720 °C Show Material materials with Vicat softening temperature of 1590 - 1720 °C |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant | 23.0 °C | 3.7 - 3.9 [-] Show Material materials with Dielectric constant of 3.7 - 3.9 [-] | at 500MHz |
Loss factor | 23.0 °C | 4E-4 - 1E-3 [-] Show Material materials with Loss factor of 4E-4 - 1E-3 [-] |
Optical
| Property | Value |
|---|---|
Abbe number | 67.6 - 67.84 [-] Show Material materials with Abbe number of 67.6 - 67.84 [-] |
Refractive index | 1.46 [-] Show Material materials with Refractive index of 1.46 [-] |