Aluminium Alloy FA7911 O

Supplied by Gränges

A high strength, heat-treatable intermediate Mg material for header and plate applications suited for controlled atmosphere brazing.

Chemical composition

Element Weight %
Mn 1.11.4
Si 0.60.8
Cu 0.40.6
Fe 0.40.6
Ti 0.10.2
Mg 0.10.2
Zn 0.00.05


Elongation A50, A50
18.00 %
Tensile strength, Rm
130.00—170.00 MPa
Yield strength Rp0.2, Rp0.2
45.00 MPa
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.

Technological properties

Corrosion properties
Corrosion potential after brazing -690 mV vs SCE
Standard process capabilities: width 10-1400mm; thickness 0.050-3.18mm
With a combination of good formability and high post braze strength, FA7911 is highly suitable for the use in headers and plates. The defined composition of silicon and magnesium makes FA7911 easy to braze in the CAB process, while showing good ageing behaviour after brazing. The addition of titanium to the product also enables a very good corrosion protection. In typical header and plate dimensions it easily exceeds 60 days of SWAAT life without perforations. FA7911 exhibits excellent corrosion performance with lateral corrosion behavior in SWAAT (ASTM G85). The corrosion attack is proceeding horizontally and prolonging the time to perforation. The addition of titanium improves the corrosion behavior of the bulk material by hindering pitting corrosion.
Processing history
Temper: O
This material data has been provided by Gränges.


Gränges develops, produces, and distributes rolled aluminum material for brazed heat exchanger applications in the Americas, Europe, and Asia.

View full profile


Similar Materials

These are materials almost identical to the ones you are looking at. They could be a relevant standard or a different supplier.

Go to to find materials similar to Aluminium Alloy FA7911 O.