ОоА prepreg B180 CF02 [0,+45]nS

Want to keep this datasheet? Save it now in your required format

Description

В180 is a prepreg based on epoxy carbon fiber reinforced resin for producing details with operating temperatures up to 150°C. Out-of-autoclave prepreg technology has the most advantages of autoclave. The autoclave is not required for processing the prepreg B180. Curing takes place in a vacuum bag, with the technology of the package laminating slightly different from the vacuum infusion. It shows the following features and properties:

High mechanical performance

Possibility of application in loaded parts at service temperatures up to 120°C

Less stringent requirements for working staff

Glass transition temperature 154°C

Out of autoclave processing

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

Mechanical

Property	Temperature	Value	Comment
Compressive modulus	23.0 °C	60 MPa Show Material materials with Compressive modulus of 60 MPa	ASTM D695, Lamina
Compressive strength	23.0 °C	802 MPa Show Material materials with Compressive strength of 802 MPa	ASTM D6641, Lamina
Compressive strength laminate	25.0 °C	708 MPa Show Material materials with Compressive strength laminate of 708 MPa
	85.0 °C	639 MPa Show Material materials with Compressive strength laminate of 639 MPa

Elastic modulus	23.0 °C	71 GPa Show Material materials with Elastic modulus of 71 GPa	ASTM D3039, Lamina
Shear strength, τ₁₂	23.0 °C	126 MPa Show Material materials with Shear strength, τ₁₂ of 126 MPa
Tensile strength	23.0 °C	871 MPa Show Material materials with Tensile strength of 871 MPa	ASTM D3039, Lamina

Technological properties

Property
Application areas	Marine: The shells of boats and sport catamarans can be made of composites;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite
Processing history	Reinforcing filler: carbon fabric 22502 (twill 2x2, 200 g/m2, HTA40). Carbon plastic is produced by vacuum molding.
Processing methods	Holding at a temperature of 25-30°C, for 12 hours, a vacuum of -1 bar. Heating 2°C/min. up to 120°C, holding at 120°C for 180 minutes. Heating 2°C/min. up to 180°C, holding at 180°C for 180 minutes, cooling no faster than 5°C/min. up to 50°С.