Epoxy resin T20-60 (EP-CF)

Want to keep this datasheet? Save it now in your required format

Description

T20-60 is a two-part low viscosity epoxy infusion carbon fiber reinforced resin developed for mass CFRP production. The resin offers simple and flexible processing due to low viscosity and room temperature impregnation. T20-60 was developed specially for vacuum infusion molding, to produce laminates with low porosity and optimal mechanical performance. It shows the following features and properties:

Two-part resin system for vacuum infusion and RTM

Wide processing window > 2 hours at 25°C

Curing at room temperature

Low exotherm

High crack resistance

Optimal price/quality ratio

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

Mechanical

Property	Temperature	Value	Comment
Compressive modulus	25.0 °C	61 MPa Show Material materials with Compressive modulus of 61 MPa	ASTM D695
	80.0 °C	56 MPa Show Material materials with Compressive modulus of 56 MPa	ASTM D695

Compressive strength	25.0 °C	583 MPa Show Material materials with Compressive strength of 583 MPa	ASTM D6641
	80.0 °C	460 MPa Show Material materials with Compressive strength of 460 MPa	ASTM D6641
	Unlock all property charts
Elastic modulus	23.0 °C	61 GPa Show Material materials with Elastic modulus of 61 GPa	ASTM D3039
Shear modulus, G₁₂	25.0 °C	4.1 GPa Show Material materials with Shear modulus, G₁₂ of 4.1 GPa	ASTM D5379
	80.0 °C	2.5 GPa Show Material materials with Shear modulus, G₁₂ of 2.5 GPa	ASTM D5379
	Unlock all property charts
Shear strength, τ₁₂	25.0 °C	110 MPa Show Material materials with Shear strength, τ₁₂ of 110 MPa
	80.0 °C	56 MPa Show Material materials with Shear strength, τ₁₂ of 56 MPa
	Unlock all property charts
Shear strength, τ₁₃	25.0 °C	58 MPa Show Material materials with Shear strength, τ₁₃ of 58 MPa	ASTM D2344
	80.0 °C	36 MPa Show Material materials with Shear strength, τ₁₃ of 36 MPa	ASTM D2344
	Unlock all property charts
Tensile strength	23.0 °C	777 MPa Show Material materials with Tensile strength of 777 MPa	ASTM D3039

Technological properties

Property
Application areas	Marine: The shells of boats and sport catamarans can be made of composite;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Wind energy: Wind turbines is usually made of carbon fiber plastic;Design;Room temperature tooling;High-pressure cylinders
Processing history	Samples for testing were obtained by vacuum infusion based on T20-60 resin and carbon fabric 22502 (twill 2x2, 200 g/m2, 3K, 3.95 GPa).
Processing methods	Mix the components A and B and weight proportion 100:32. Degas the resin with intensive mixing for 15-20 minutes at 20-25°С. Maintaining resin pot temperature of 20-25°С and tool temperature of 20-25°С, begin resin infusion. Cure at room temperature for 24h. Make sure the resin is gelled. Remove auxiliary materials. Increase temperature at rate 0,5-2°С/min to 80°С. Postcure at 80°С for 3-6h.