Reinforced with 68% Carbon Fibers

Ashby charts



Density ρ

1.6 g/cm³ at 20 °C


Elastic modulus E

240 GPa at 20 °C

Elongation A

1.7 % at 20 °C

Poisson's ratio ν

0.25 [-] at 20 °C

Shear strength τ

40 MPa at 20 °C

Tensile strength Rm

3400 MPa at 20 °C

Technological properties

Processing methods

The production process is formed by laminating hot-pressed carbon fiber prepreg.

This material data has been provided by Jinjiuyi Carbon Fiber Team.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.