LEXAN™ Resin 241S

Want to keep this datasheet? Save it now in your required format

Description

10.5 MFR. Improved flame retardance. Super mold release.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Material materials with Density of 1.19 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.15 %

Show Material materials with Water absorption of 0.15 %

ASTM D 570 | 24 Hours

Water absorption, equilibrium

100.0 °C

0.58 %

Show Material materials with Water absorption, equilibrium of 0.58 %

ASTM D 570 | ASTM D 570

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

130 %

Show Material materials with Elongation of 130 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

7 %

Show Material materials with Elongation at yield of 7 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.34 GPa

Show Material materials with Flexural modulus of 2.34 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural yield strength

23.0 °C

96 MPa

Show Material materials with Flexural yield strength of 96 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Hardness, Rockwell M

23.0 °C

70 [-]

Show Material materials with Hardness, Rockwell M of 70 [-]

ASTM D 785

Hardness, Rockwell R

23.0 °C

118 [-]

Show Material materials with Hardness, Rockwell R of 118 [-]

ASTM D 785

Impact strength, Izod notched, ASTM

23.0 °C

801 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 801 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

3204 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m

ASTM D 4812

Tensile strength

23.0 °C

68 MPa

Show Material materials with Tensile strength of 68 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

62 MPa

Show Material materials with Yield strength of 62 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.84E-5 1/K

Show Material materials with Coefficient of thermal expansion of 6.84E-5 1/K

ASTM E 831 | -40°C to 95°C

Heat deflection temperature, 1.80 MPa

132 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 132 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Relative temperature index, electrical

130 °C

Show Material materials with Relative temperature index, electrical of 130 °C

UL 746B

Relative temperature index, mechanical impact

130 °C

Show Material materials with Relative temperature index, mechanical impact of 130 °C

UL 746B

Relative temperature index, mechanical strength

130 °C

Show Material materials with Relative temperature index, mechanical strength of 130 °C

UL 746B

Specific heat capacity

23.0 °C

1250 J/(kg·K)

Show Material materials with Specific heat capacity of 1250 J/(kg·K)

ASTM C 351

Thermal conductivity

23.0 °C

0.27 W/(m·K)

Show Material materials with Thermal conductivity of 0.27 W/(m·K)

ASTM C177

Vicat softening temperature

154 °C

Show Material materials with Vicat softening temperature of 154 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94V-0 Flame Class Rating | 5.99mm | UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

2 V

Show Material materials with Comparative tracking index of 2 V

UL 746A

Dielectric constant

23.0 °C

2.96 [-]

Show Material materials with Dielectric constant of 2.96 [-]

ASTM D 150 | at 1 MHz

Dielectric strength

23.0 °C

14.9 kV/mm

Show Material materials with Dielectric strength of 14.9 kV/mm

ASTM D 149 | in air, 3.2 mm

Dissipation factor

23.0 °C

0.01 [-]

Show Material materials with Dissipation factor of 0.01 [-]

ASTM D 150 | at 1 MHz

Optical

PropertyValueComment

Haze

1 %

Show Material materials with Haze of 1 %

ASTM D 1003 | 2.54 mm

Refractive index

1.59 [-]

Show Material materials with Refractive index of 1.59 [-]

ASTM D542

Transmission

88 %

Show Material materials with Transmission of 88 %

ASTM D 1003 | 2.54 mm

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

10.5 g/10min

Show Material materials with Melt mass-flow rate of 10.5 g/10min

ASTM D 1238 | 300°C/1.2 kg

Shrinkage

23.0 °C

0.5 - 0.7 %

Show Material materials with Shrinkage of 0.5 - 0.7 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Building Element,Electronic Components,Enclosures,Power Manangement,Wiring Devices

Processing methods

Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm