LEXAN™ FR Resins BY2710X

Want to keep this datasheet? Save it now in your required format

Description

LEXAN BY2710X Polycarbonate (PC) is an injection moldable non-chlorinated/brominated, unfilled, flame retardant grade with good flow and impact performance. It has an MVR of 15 (300°C/1.2kg), UL94 V0@1.5mm, is available in various opaque color options.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.22 GPa Show Material materials with Elastic modulus of 2.22 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	100 % Show Material materials with Elongation of 100 %	ASTM D 638 \| Type I, 50 mm/min
Elongation at yield	23.0 °C	6 % Show Material materials with Elongation at yield of 6 %	ASTM D 638 \| Type I, 50 mm/min
Flexural modulus	23.0 °C	2.07 GPa Show Material materials with Flexural modulus of 2.07 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural yield strength	23.0 °C	90 MPa Show Material materials with Flexural yield strength of 90 MPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Impact strength, Izod notched, ASTM	23.0 °C	800 J/m Show Material materials with Impact strength, Izod notched, ASTM of 800 J/m	ASTM D 256
Tensile strength	23.0 °C	61 MPa Show Material materials with Tensile strength of 61 MPa	ASTM D 638 \| Type I, 50 mm/min
Yield strength	23.0 °C	60 MPa Show Material materials with Yield strength of 60 MPa	ASTM D 638 \| Type I, 50 mm/min

Thermal

Property	Value	Comment
Relative temperature index, electrical	130 °C Show Material materials with Relative temperature index, electrical of 130 °C	UL 746B
Relative temperature index, mechanical impact	115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C	UL 746B
Relative temperature index, mechanical strength	125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C	UL 746B
Vicat softening temperature	139 °C Show Material materials with Vicat softening temperature of 139 °C	ASTM D 1525 \| Rate B/50
Flammability	UL Recognized, 94V-0 Flame Class Rating \| 1.5mm \| UL 94

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		15 g/10min Show Material materials with Melt mass-flow rate of 15 g/10min	ASTM D 1238 \| 300°C/1.2 kg
Shrinkage	23.0 °C	0.6 - 0.8 % Show Material materials with Shrinkage of 0.6 - 0.8 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Data Transfer,Displays,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,Personal Computing,Power Manangement,Wireless Communications,Wiring Devices
Processing methods	Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm