General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.94 % Show Material materials with Water absorption of 0.94 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Material materials with Elastic modulus of 3.1 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 38 % Show Material materials with Elongation of 38 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 21 % Show Material materials with Elongation at yield of 21 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 2.9 GPa Show Material materials with Flexural modulus of 2.9 GPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 92 [-] Show Material materials with Hardness, Rockwell M of 92 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 300 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 300 kJ/m² | ISO 179/1eU |
23.0 °C | 350 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 350 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Yield strength | 23.0 °C | 72 MPa Show Material materials with Yield strength of 72 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 158 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 158 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 97 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 97 °C | ISO 75-1/-2 | |||
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat softening temperature | 175 °C Show Material materials with Vicat softening temperature of 175 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 28 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 100Hz of 3.9 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 1MHz of 3.9 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 44 kV/mm Show Material materials with Dielectric strength of 44 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 5E-4 [-] Show Material materials with Dissipation factor, 100Hz of 5E-4 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 5.5E-3 [-] Show Material materials with Dissipation factor, 1MHz of 5.5E-3 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 5.00E+13 Ω/sq Show Material materials with Surface resistivity of 5.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 2.5 g/10min Show Material materials with Melt mass-flow rate of 2.5 g/10min | ISO 1133 | 190°C/2.16kg | |
Melt volume-flow rate | 2.1 cm³/10min Show Material materials with Melt volume-flow rate of 2.1 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 2.2 % Show Material materials with Shrinkage of 2.2 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.8 % Show Material materials with Shrinkage, transverse of 1.8 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 8s/mm |