Crastin® SK615SF BK591

Alternative and trade names
PBT-GF30

Want to keep this datasheet? Save it now in your required format

Description

ISO 7792-PBT,MGNR,09-100,GF30Common features of Crastin® thermoplastic polyester resin include mechanical and physical properties such as stiffness and toughness, heat resistance, friction and wear resistance, excellent surface finishes and good colourability. Crastin® thermoplastic polyester resin has excellent electrical insulation characteristics and high arc-resistant grades are available. Many flame retardant grades have UL recognition (class V-0). Crastin® thermoplastic polyester resin typically has high chemical and heat ageing resistance. The good melt stability of Crastin® thermoplastic polyester resin normally enables the recycling of properly handled production waste.If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-24 kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed. Crastin® thermoplastic polyester resin typically is used in demanding applications in the electronics, electrical, automotive, mechanical engineering, chemical, domestic appliances and sporting goods industry.Crastin® SK615SF is a 30% glass fiber reinforced, low viscosity polybutylene terephtalate for injection molding. It has high flow characteristics and is specifically suitable for super fast production. It is laser markable.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.53 g/cm³ Show Material materials with Density of 1.53 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	9.9 GPa Show Material materials with Elastic modulus of 9.9 GPa	ISO 527-1/-2
Elongation	23.0 °C	2.5 % Show Material materials with Elongation of 2.5 %	ISO 527-1/-2
Impact strength, Charpy notched	23.0 °C	9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m²	ISO 179/1eA
Poisson's ratio	23.0 °C	0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-]
Tensile strength	23.0 °C	145 MPa Show Material materials with Tensile strength of 145 MPa	ISO 527-1/-2

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C	ISO 75-1/-2
Melting point	222 °C Show Material materials with Melting point of 222 °C	ISO 11357-1/-3 \| 18°F/min
Flammability	Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, Glow Wire Flammability Index, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 78 mm/min

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.3 % Show Material materials with Shrinkage of 0.3 %	ISO 294-4, 2577
Shrinkage, transverse	23.0 °C	1.1 % Show Material materials with Shrinkage, transverse of 1.1 %	ISO 294-4, 2577

Technological properties

Property
Fillers	30% Glass Fiber
Processing methods	Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 240°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C

Crastin® SK615SF BK591

Description

Ashby charts

Suggested reading

Properties