Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.27 GPa Show Material materials with Elastic modulus of 0.27 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 450 % Show Material materials with Elongation of 450 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.29 GPa Show Material materials with Flexural modulus of 0.29 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 58 [-] Show Material materials with Hardness, Shore D of 58 [-] | ISO 7619-1 | 15 seconds | ||
Impact strength, Charpy notched | -40.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
-6.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | No Break @ 23°C, ISO 179/1eU | |||
Poisson's ratio | 23.0 °C | 0.48 [-] Show Material materials with Poisson's ratio of 0.48 [-] | |||
Tear strength | 23.0 °C | 180 kN/m Show Material materials with Tear strength of 180 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 150 kN/m Show Material materials with Tear strength, transverse of 150 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 41 MPa Show Material materials with Tensile strength of 41 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23°C, ISO 179/1eU |
Thermal
Property | Value | Comment | |
---|---|---|---|
Melting point | 212 °C Show Material materials with Melting point of 212 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat softening temperature | 187 °C Show Material materials with Vicat softening temperature of 187 °C | ISO 306 | 90°F, 2 lbf | |
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 5 g/10min Show Material materials with Melt mass-flow rate of 5 g/10min | ISO 1133 | 230°C/10kg | |
Melt volume-flow rate | 5 cm³/10min Show Material materials with Melt volume-flow rate of 5 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.9 % Show Material materials with Shrinkage of 1.9 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 2.1 % Show Material materials with Shrinkage, transverse of 2.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |