Polycarbonate Reinforced with 30% Glass Fibers (PC+GF30)

Alternative and trade names
Makrolon®, Lexan®
.XLSX
.PDF
Save

Description

Reinforced poylcarbonate with 30% glass fiber.


  • High viscosity
  • Easy release extrusion
  • Properties

    General

    Density ρ

    1.35 - 1.46 g/cm³ at 20 °C

    Mechanical

    Elastic modulus E

    6 - 9 GPa at 20 °C

    Elongation A

    1 - 3.5 % at 20 °C

    Impact strength, Charpy notched Ivnot

    4 - 17 kJ/m² at 20 °C

    Impact strength, Charpy unnotched Iunnot

    30 - 60 kJ/m² at 20 °C

    Max allowed stress σmax

    60 - 160 MPa at 20 °C

    at 1-3.5% strain

    Thermal

    Coefficient of thermal expansion α

    2E-5 - 7E-5 1/K at 20 °C

    Flammability

    UL 94 V2-V0

    Max service temperature, long Tmaxlong

    115 - 130 °C

    Max service temperature, short Tmaxshort

    115 - 150 °C

    Specific heat capacity cp

    1100 J/(kg·K) at 20 °C

    Thermal conductivity λ

    0.24 W/(m·K) at 20 °C

    Electrical

    Dielectric constant εr

    3.1 - 3.6 [-] at 20 °C

    Electrical resistivity ρel

    1.00E+13 - 1.00E+14 Ω·m at 20 °C

    Optical

    Transparency

    no

    Technological properties

    Application areas

    Housing parts

    Fillers

    30% Glass Fiber

    Processing methods

    Injection molding

    This material data has been provided by M-Base.

    All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
    Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.