DIN 1725-1 Grade 3.3318 F

Want to keep this datasheet? Save it now in your required format

Description

The alloy Al99,9Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents from the degree of purity of the alloy and the thickness of the produced anodising layer. The alloy Al99,9Mg1 is nature hard, i.e. with their a strength increase can be achieved only by cold forming. The material is well cold and warm fomrable, has a very good corrosion resistance and is also well anodically to be oxidized. Application: For metal goods, like building fittings, table-ware, flow pressed parts, autotrim and divides and for decoration and jeweller goods.

Related Standards

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

20.0 °C

70.0

Show Material materials with Elastic modulus of 70.0

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Elongation

20.0 °C

13.0 %

Show Material materials with Elongation of 13.0 %

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

A10

20.0 °C

15.0 %

Show Material materials with Elongation of 15.0 %

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Hardness, Brinell

20.0 °C

30.0 [-]

Show Material materials with Hardness, Brinell of 30.0 [-]

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

20.0 °C

26.0

Show Material materials with Shear modulus of 26.0

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Tensile strength

20.0 °C

100.0 MPa

Show Material materials with Tensile strength of 100.0 MPa

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Thermal

PropertyValueComment

Coefficient of thermal expansion

2.2e-05 - 2.5e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.2e-05 - 2.5e-05 1/K

Typical for Wrought 5000 Series Aluminium

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

560.0 - 655.0 °C

Show Material materials with Melting point of 560.0 - 655.0 °C

Typical for Wrought 5000 Series Aluminium

Specific heat capacity

879.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K)

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

112.0 - 205.0 W/(m·K)

Show Material materials with Thermal conductivity of 112.0 - 205.0 W/(m·K)

Typical for Wrought 5000 Series Aluminium

Electrical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Electrical conductivity

20.0 °C

33000000.0

Show Material materials with Electrical conductivity of 33000000.0

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Electrical resistivity

3.3e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m

Typical for Wrought 5000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Iron

0.04

Show Material materials with Iron of 0.04

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Magnesium

0.8 - 1.1 %

Show Material materials with Magnesium of 0.8 - 1.1 %

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Manganese

0.03

Show Material materials with Manganese of 0.03

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Silicon

0.06

Show Material materials with Silicon of 0.06

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Titanium

0.01

Show Material materials with Titanium of 0.01

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Zinc

0.04

Show Material materials with Zinc of 0.04

F

DIN 1725-1, EN 573-3, EN 573-4

Profile

Technological properties

Property
Workability

Good workability.