DIN 1725-1 Grade 3.2307 T6

Want to keep this datasheet? Save it now in your required format

Description

The alloy Al99,85MgSi belongs to the standardised aluminum shining materials. Aluminum alloys being based on aluminum with a minimum purity of 99,85 %, can be polished after mechanical polishing chemically or electrolytically to high gloss. The produced gloss degree must, in order to remain preserved, be afterwards anodised. The degree of arranged reflection depends again on the degree of purity and the anodising layer thickness. The alloy Al99,85MgSi belongs due to its composition to the hardenable shining materials. It is cold and hot hardenable. Strength grade up to F 24 can be achieved by hot hardening. The alloy Al99,85MgSi has a very good corrosion resistance and is well cold and/or warm formable. This alloy is standardised only as extruded section (DIN 1748 T1 and T2) and piece of drop forge (DIN 1749 T1 and T2). Application: For decoration goods and/or Bijouterie articles for metal goods of all kinds (e.g. building fittings, table-ware, flow pressed parts) and for reflectors.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

70.0 GPa

Show Material materials with Elastic modulus of 70.0 GPa

Typical for Wrought 6000 Series Aluminium

Elongation

20.0 °C

14.0 %

Show Material materials with Elongation of 14.0 %

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Hardness, Brinell

20.0 °C

70.0 [-]

Show Material materials with Hardness, Brinell of 70.0 [-]

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 6000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 6000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 6000 Series Aluminium

Tensile strength

20.0 °C

235.0 MPa

Show Material materials with Tensile strength of 235.0 MPa

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Thermal

PropertyValueComment

Coefficient of thermal expansion

1.6e-05 - 2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K

Typical for Wrought 6000 Series Aluminium

Melting point

555.0 - 655.0 °C

Show Material materials with Melting point of 555.0 - 655.0 °C

Typical for Wrought 6000 Series Aluminium

Specific heat capacity

887.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K)

Typical for Wrought 6000 Series Aluminium

Thermal conductivity

170.0 - 220.0 W/(m·K)

Show Material materials with Thermal conductivity of 170.0 - 220.0 W/(m·K)

Typical for Wrought 6000 Series Aluminium

Electrical

PropertyValueComment

Electrical conductivity

21000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 21000000.0 - 34000000.0 S/m

Typical for Wrought 6000 Series Aluminium

Electrical resistivity

2.9e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 2.9e-08 - 5e-08 Ω·m

Typical for Wrought 6000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Copper

0.05 - 0.2 %

Show Material materials with Copper of 0.05 - 0.2 %

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Iron

0.08

Show Material materials with Iron of 0.08

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Magnesium

0.35 - 0.7 %

Show Material materials with Magnesium of 0.35 - 0.7 %

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Manganese

0.03

Show Material materials with Manganese of 0.03

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Silicon

0.35 - 0.7 %

Show Material materials with Silicon of 0.35 - 0.7 %

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Titanium

0.02

Show Material materials with Titanium of 0.02

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Zinc

0.05

Show Material materials with Zinc of 0.05

T6

DIN 1725-1, EN 573-3, EN 573-4

Forging

Technological properties

Property
Workability

Excellent workability.