General
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 130.0 MPa Show Material materials with Bending Fatigue Strength of 130.0 MPa | T4 | EN 573-3, EN 485, EN 755 | |||
Bending angle 180° | 3.0 °/t Show Material materials with Bending angle 180° of 3.0 °/t | T4 | EN 573-3, EN 485 | |||
5.0 °/t Show Material materials with Bending angle 180° of 5.0 °/t | T4 | EN 573-3, EN 485 | ||||
Bending angle 90° | 3.0 °/t Show Material materials with Bending angle 90° of 3.0 °/t | T4 | EN 573-3, EN 485 | |||
5.0 °/t Show Material materials with Bending angle 90° of 5.0 °/t | T4 | EN 573-3, EN 485 | ||||
8.0 °/t Show Material materials with Bending angle 90° of 8.0 °/t | T4 | EN 573-3, EN 485 | ||||
Elastic modulus | 72.5 GPa Show Material materials with Elastic modulus of 72.5 GPa | T4 | EN 573-3, EN 1301, EN 485, EN 755 | |||
20.0 °C | 65.0 - 73.5 GPa Show Material materials with Elastic modulus of 65.0 - 73.5 GPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging, Wire | ||
Elongation | 2.0 % Show Material materials with Elongation of 2.0 % | T4 | EN 573-3, EN 485 | A100 | ||
4.0 % Show Material materials with Elongation of 4.0 % | T4 | EN 573-3, EN 485 | A100 | |||
6.0 % Show Material materials with Elongation of 6.0 % | T4 | EN 573-3, EN 485 | A100 | |||
7.0 % Show Material materials with Elongation of 7.0 % | T4 | EN 573-3, EN 485, EN 755 | A100 | |||
8.0 % Show Material materials with Elongation of 8.0 % | T4 | EN 573-3, EN 755 | A100 | |||
8.0 % Show Material materials with Elongation of 8.0 % | T4 | EN 573-3, EN 755 | A50 | |||
9.0 % Show Material materials with Elongation of 9.0 % | T4 | EN 573-3, EN 755 | A100 | |||
10.0 % Show Material materials with Elongation of 10.0 % | T4 | EN 573-3, EN 755 | A100 | |||
10.0 % Show Material materials with Elongation of 10.0 % | T4 | EN 573-3, EN 755 | A50 | |||
12.0 % Show Material materials with Elongation of 12.0 % | T4 | EN 573-3, EN 485, EN 755 | A100 | |||
13.0 % Show Material materials with Elongation of 13.0 % | T4 | EN 573-3, EN 485 | A50 | |||
14.0 % Show Material materials with Elongation of 14.0 % | T4 | EN 573-3, EN 485 | A50 | |||
15.0 % Show Material materials with Elongation of 15.0 % | T4 | EN 573-3, EN 485 | A50 | |||
18.0 % Show Material materials with Elongation of 18.0 % | T4 | EN 573-3, EN 1301 | ||||
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | A100 | |
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | A10 | |
20.0 °C | 10.0 % Show Material materials with Elongation of 10.0 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging | ||
Hardness, Brinell | 101.0 [-] Show Material materials with Hardness, Brinell of 101.0 [-] | T4 | EN 573-3, EN 485 | |||
105.0 [-] Show Material materials with Hardness, Brinell of 105.0 [-] | T4 | EN 573-3, EN 485 | ||||
108.0 [-] Show Material materials with Hardness, Brinell of 108.0 [-] | T4 | EN 573-3, EN 485 | ||||
110.0 [-] Show Material materials with Hardness, Brinell of 110.0 [-] | T4 | EN 573-3, EN 485 | ||||
111.0 [-] Show Material materials with Hardness, Brinell of 111.0 [-] | T4 | EN 573-3, EN 485 | ||||
20.0 °C | 95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging | ||
20.0 °C | 100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.2 GPa Show Material materials with Shear modulus of 27.2 GPa | T4 | EN 573-3, EN 1301, EN 485, EN 755 | |||
20.0 °C | 26.0 - 28.5 GPa Show Material materials with Shear modulus of 26.0 - 28.5 GPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging, Wire | ||
Shear strength | 20.0 °C | 260.0 MPa Show Material materials with Shear strength of 260.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | |
Tensile strength | 300.0 MPa Show Material materials with Tensile strength of 300.0 MPa | T4 | EN 573-3, EN 485 | |||
330.0 MPa Show Material materials with Tensile strength of 330.0 MPa | T4 | EN 573-3, EN 485 | ||||
350.0 MPa Show Material materials with Tensile strength of 350.0 MPa | T4 | EN 573-3, EN 485 | ||||
360.0 MPa Show Material materials with Tensile strength of 360.0 MPa | T4 | EN 573-3, EN 485, EN 755 | ||||
370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T4 | EN 573-3, EN 485, EN 755 | ||||
380.0 MPa Show Material materials with Tensile strength of 380.0 MPa | T4 | EN 573-3, EN 1301, EN 755 | ||||
385.0 MPa Show Material materials with Tensile strength of 385.0 MPa | T4 | EN 573-3, EN 485 | ||||
390.0 MPa Show Material materials with Tensile strength of 390.0 MPa | T4 | EN 573-3, EN 485, EN 755 | ||||
400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T4 | EN 573-3, EN 755 | ||||
20.0 °C | 380.0 MPa Show Material materials with Tensile strength of 380.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging, Wire | ||
20.0 °C | 436.0 MPa Show Material materials with Tensile strength of 436.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | |||
100.0 °C | 394.0 MPa Show Material materials with Tensile strength of 394.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | |||
150.0 °C | 281.0 MPa Show Material materials with Tensile strength of 281.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | |||
200.0 °C | 155.0 MPa Show Material materials with Tensile strength of 155.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | |||
250.0 °C | 84.0 MPa Show Material materials with Tensile strength of 84.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | |||
300.0 °C | 46.0 MPa Show Material materials with Tensile strength of 46.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | |||
370.0 °C | 32.0 MPa Show Material materials with Tensile strength of 32.0 MPa | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T4 | EN 573-3, EN 1301, EN 485, EN 755 | |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T4 | EN 573-3, EN 1301, EN 485, EN 755 | ||
Melting point | 512.0 - 650.0 °C Show Material materials with Melting point of 512.0 - 650.0 °C | T4 | EN 573-3, EN 1301, EN 485, EN 755 | ||
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K) | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging, Wire |
Thermal conductivity | 20.0 °C | 130.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 200.0 W/(m·K) | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 28000000.0 S/m | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Electrical resistivity | 3.57e-08 - 5.56e-08 Ω·m Show Material materials with Electrical resistivity of 3.57e-08 - 5.56e-08 Ω·m | T4 | EN 573-3, EN 1301, EN 485, EN 755 |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Copper | 3.5 - 4.5 % Show Material materials with Copper of 3.5 - 4.5 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Iron | 0.7 % Show Material materials with Iron of 0.7 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Forging, Wire |
0.70 % Show Material materials with Iron of 0.70 % | T4 | EN 573-3, EN 1301, EN 485, EN 755 | ||
Magnesium | 0.4 - 1.0 % Show Material materials with Magnesium of 0.4 - 1.0 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Silicon | 0.2 - 0.8 % Show Material materials with Silicon of 0.2 - 0.8 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T4 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 1301, EN 485, EN 755 | Forging, Wire |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not suitable, Protective: good | |
Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable | |
Corrosion properties | Seawater: poor, weathering: sufficient | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) acceptable (O) / acceptable (O) |