EN 573-1 Grade AW-5049 H111

Want to keep this datasheet? Save it now in your required format

Description

Universal work hardening alloy offering medium strength, very good formability, very good corrosion resistance, and good durability.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-1 Grade AW-5049 H111 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.7 - 2.71 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Thickness

t

0.2 - 6 mm

Mechanical

Bending angle 180°

θ180

0.5 - 1 °/t at 20 °C

Show 5000 Series materials with Bending angle 180° of 0.5 - 1 °/t at 20 °C

Bending angle 90°

θ90

0 - 2 °/t at 20 °C

Show 5000 Series materials with Bending angle 90° of 0 - 2 °/t at 20 °C

Elastic modulus

E

70 GPa at -270 °C

Show 5000 Series materials with Elastic modulus of 70 GPa at -270 °C

Hide chart

Elongation

A

17 - 18 % at 20 °C

Show 5000 Series materials with Elongation of 17 - 18 % at 20 °C

Elongation A100

A100

17 % at 20 °C

Show 5000 Series materials with Elongation A100 of 17 % at 20 °C

Elongation A50

A50

12 - 18 % at 20 °C

Show 5000 Series materials with Elongation A50 of 12 - 18 % at 20 °C

Elongation A50, transverse

A50,trans

12 - 18 % at 20 °C

Show 5000 Series materials with Elongation A50, transverse of 12 - 18 % at 20 °C

Elongation, transverse

A

17 % at 20 °C

Show 5000 Series materials with Elongation, transverse of 17 % at 20 °C

Hardness, Brinell

HB

50 - 52 [-] at 20 °C

Show 5000 Series materials with Hardness, Brinell of 50 - 52 [-] at 20 °C

Hardness, HBW

HBW

52 [-] at 20 °C

Show 5000 Series materials with Hardness, HBW of 52 [-] at 20 °C

Impact strength, Charpy notched

Ivnot

30 kJ/m² at 20 °C

Show 5000 Series materials with Impact strength, Charpy notched of 30 kJ/m² at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 5000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 5000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

G

26.5 GPa at 20 °C

Show 5000 Series materials with Shear modulus of 26.5 GPa at 20 °C

Tensile strength

Rm

180 - 250 MPa at 20 °C

Show 5000 Series materials with Tensile strength of 180 - 250 MPa at 20 °C

Tensile strength, transverse

Rm,trans

190 - 240 MPa at 20 °C

Show 5000 Series materials with Tensile strength, transverse of 190 - 240 MPa at 20 °C

Yield strength

YS

80 MPa at 20 °C

Show 5000 Series materials with Yield strength of 80 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

80 MPa at -270 °C

Show 5000 Series materials with Yield strength Rp0.2 of 80 MPa at -270 °C

Unlock all property charts

Yield strength Rp0.2, transverse

Rp0.2,trans

80 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2, transverse of 80 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.37E-5 1/K at 20 °C

20-100°C

Unlock all property charts

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Max service temperature, long

Tmaxlong

0 - 150 °C

Melting point

Tm

620 - 650 °C

Specific heat capacity

cp

879 - 963 J/(kg·K) at 20 °C

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

λ

140 - 180 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.00E+7 - 2.50E+7 S/m at 20 °C

Electrical resistivity

ρel

4E-8 - 5E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Mg

1.6 - 2.6 %

Fe

0.5 - 0.7 %

Mn

0.5 - 1.1 %

Si

0.4 %

Cr

0.3 %

More

Technological properties

Anodizing

Excellent (anodizing quality)

Application areas

Components: General trasportation

Brazing

Poor

Corrosion properties

Excellent

Welding

Very Good

Workability

Very Good (in O temper)

This material data has been provided by Aludium,WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.