EN 10292 Grade HX340LAD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated

Want to keep this datasheet? Save it now in your required format

Description

The steel HX340LAD (X=roll condition, LA=low alloyed, D=hot-dip coatable) is producible with the following coatings: - HX340LAD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side) - HX340LAD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side) - HX340LAD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side) - HX340LAD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side) - HX340LAD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side) The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side). Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled. Mechanical properties are warranted for a period of 3 months for Bake-hardening steels and for a period of 6 months after provision of the products for all other sorts. The same terms are valid for freedom from stretcher strains (surface type B and C). It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures. Furthermore suitability for joining by sticking as well as for application of organic coatings. Application: household appliances industry, construction trade, electrical industry, furniture industry, car industry.,The steel HX340LAD (X=roll condition, LA=low alloyed, D=hot-dip coatable) is deliverable with the following coatings: - HX340LAD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side) - HX340LAD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side) - HX340LAD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side) - HX340LAD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side) - HX340LAD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side) The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side). Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled. Mechanical properties are warranted for a period of 6 months after provision. The same time is valid for freedom from stretcher strains (surface type B and C). It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures. Furthermore suitability for joining by sticking as well as for application of organic coatings. Application: household appliances industry, construction trade, electrical industry, furniture industry, car industry.

Related Standards

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValue

Elongation A80

20.0 °C

22 %

Show Material materials with Elongation A80 of 22 %

Elongation A80, transverse

20.0 °C

21 %

Show Material materials with Elongation A80, transverse of 21 %

Tensile strength

20.0 °C

400 - 500 MPa

Show Material materials with Tensile strength of 400 - 500 MPa

Tensile strength, transverse

20.0 °C

410 - 510 MPa

Show Material materials with Tensile strength, transverse of 410 - 510 MPa

Yield strength Rp0.2

20.0 °C

320 - 400 MPa

Show Material materials with Yield strength Rp0.2 of 320 - 400 MPa

Yield strength Rp0.2, transverse

20.0 °C

340 - 420 MPa

Show Material materials with Yield strength Rp0.2, transverse of 340 - 420 MPa

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Carbon

0.11 %

Show Material materials with Carbon of 0.11 %

Manganese

1 %

Show Material materials with Manganese of 1 %

Niobium

0.09 %

Show Material materials with Niobium of 0.09 %

Phosphorus

0.03 %

Show Material materials with Phosphorus of 0.03 %

Silicon

0.5 %

Show Material materials with Silicon of 0.5 %

Sulfur

0.025 %

Show Material materials with Sulfur of 0.025 %

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %