General
Property | Value | Comment |
---|---|---|
Carbon equivalent (CET) | 0.32 [-] Show Material materials with Carbon equivalent (CET) of 0.32 [-] | |
Carbon equivalent (CEV) | 0.46 [-] Show Material materials with Carbon equivalent (CEV) of 0.46 [-] | for t ≤ 50 mm plate thickness |
0.48 [-] Show Material materials with Carbon equivalent (CEV) of 0.48 [-] | for 50 < t ≤100 mm plate thickness | |
0.5 [-] Show Material materials with Carbon equivalent (CEV) of 0.5 [-] | for 100 < t ≤ 250 mm plate thickness | |
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | typical for low carbon steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 0 °C | 50 J Show Material materials with Charpy impact energy, V-notch of 50 J | min. |
Charpy impact energy, V-notch, transverse | 0 °C | 33 J Show Material materials with Charpy impact energy, V-notch, transverse of 33 J | min. |
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | typical for low carbon steel | |
Elongation | 17 % Show Material materials with Elongation of 17 % | min., Transverse | |
19 % Show Material materials with Elongation of 19 % | min. | ||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | typical for low carbon steel | |
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa | typical for low carbon steel | |
Tensile strength | 610 - 770 MPa Show Material materials with Tensile strength of 610 - 770 MPa |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.32e-05 - 1.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | typical for low carbon steel |
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | typical for carbon steel |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | typical for low carbon steel |
Specific heat capacity | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | typical for low carbon steel |
Thermal conductivity | 25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K) | typical for low carbon steel |
Electrical
Property | Value | Comment |
---|---|---|
Electrical resistivity | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | typical for carbon steel |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % | min. |
Carbon | 0.16 % Show Material materials with Carbon of 0.16 % | |
Chromium | 0.5 % Show Material materials with Chromium of 0.5 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Copper | 0.55 % Show Material materials with Copper of 0.55 % | |
Manganese | 1 - 1.7 % Show Material materials with Manganese of 1 - 1.7 % | |
Molybdenum | 0.5 % Show Material materials with Molybdenum of 0.5 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Nickel | 2 % Show Material materials with Nickel of 2 % | higher Ni content may be qualified and accepted subject to qualification during manufacturer qualification testing |
Niobium | 0.05 % Show Material materials with Niobium of 0.05 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Nitrogen | 0.025 % Show Material materials with Nitrogen of 0.025 % | the total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used, the minimum Al value and Al/N ratio do not apply |
Phosphorus | 0.025 % Show Material materials with Phosphorus of 0.025 % | |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | |
Sulfur | 0.025 % Show Material materials with Sulfur of 0.025 % | |
Titanium | 0.05 % Show Material materials with Titanium of 0.05 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Vanadium | 0.12 % Show Material materials with Vanadium of 0.12 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |