ASTM B210 Grade Alclad 3003 H113

.XLSX
.PDF
Save

Description

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.72 - 2.73 g/cm³ at 20 °C

Typical for Wrought 3000 Series Aluminium

Mechanical

Elastic modulus E

69.5 - 70 GPa at 20 °C

Typical for Wrought 3000 Series Aluminium

Fracture toughness KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio ν

0.33 [-] at 20 °C

Typical for Wrought 3000 Series Aluminium

Shear modulus G

25 - 26 GPa at 20 °C

Typical for Wrought 3000 Series Aluminium

Tensile strength Rm

90 MPa at 20 °C

Yield Strength Rp0.2, short transverse Rp0.2,shorttrans_

30 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.2E-5 - 2.4E-5 1/K at 20 °C

Typical for Wrought 3000 Series Aluminium

Melting point Tm

629 - 654 °C

Typical for Wrought 3000 Series Aluminium

Specific heat capacity cp

893 - 920 J/(kg·K) at 20 °C

Typical for Wrought 3000 Series Aluminium

Thermal conductivity λ

154 - 193 W/(m·K) at 20 °C

Typical for Wrought 3000 Series Aluminium

Electrical

Electrical conductivity σel

2.30E+7 - 2.90E+7 S/m at 20 °C

Typical for Wrought 3000 Series Aluminium

Electrical resistivity ρel

3.4E-8 - 4.2E-8 Ω·m at 20 °C

Typical for Wrought 3000 Series Aluminium

Chemical properties

Element

Weight %

Comment

Mn

1 - 1.5 %

Fe

0.7 %

Si

0.6 %

Zn

0.1 %

Cu

0.05 - 0.2 %

Technological properties

Workability

Good workability.

This material data has been provided by ASTM.