ASTM B241 Grade 5086 H112; Area through 20000 mm2

.XLSX
.PDF
Save

Description

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.65 - 2.7 g/cm³ at 20 °C

Typical for Wrought 5000 Series Aluminium

Mechanical

Elastic modulus E

69 - 70 GPa at 20 °C

Typical for Wrought 5000 Series Aluminium

Elongation A

10 % at 20 °C

Elongation A50 A50

12 % at 20 °C

Fracture toughness KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio ν

0.33 [-] at 20 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus G

26 - 26.5 GPa at 20 °C

Typical for Wrought 5000 Series Aluminium

Tensile strength Rm

240 MPa at 20 °C

Yield Strength Rp0.2, short transverse Rp0.2,shorttrans_

95 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.2E-5 - 2.5E-5 1/K at 20 °C

Typical for Wrought 5000 Series Aluminium

Max service temperature Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point Tm

600 - 650 °C

Typical for Wrought 5000 Series Aluminium

Specific heat capacity cp

879 - 963 J/(kg·K) at 20 °C

Typical for Wrought 5000 Series Aluminium

Thermal conductivity λ

112 - 205 W/(m·K) at 20 °C

Typical for Wrought 5000 Series Aluminium

Electrical

Electrical conductivity σel

1.80E+7 - 3.10E+7 S/m at 20 °C

Typical for Wrought 5000 Series Aluminium

Electrical resistivity ρel

3.3E-8 - 5E-8 Ω·m at 20 °C

Typical for Wrought 5000 Series Aluminium

Chemical properties

Element

Weight %

Comment

Mg

3.5 - 4.5 %

Fe

0.5 %

Si

0.4 %

Zn

0.25 %

Mn

0.2 - 0.7 %

More

Technological properties

Workability

Good workability.

This material data has been provided by ASTM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.