General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.2 - 7.34 g/cm³ Show Material materials with Density of 7.2 - 7.34 g/cm³ | Typical for Malleable Cast Iron |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 165 - 180 GPa Show Material materials with Elastic modulus of 165 - 180 GPa | Typical for Malleable Cast Iron |
Elongation | 20.0 °C | 8 - 15 % Show Material materials with Elongation of 8 - 15 % | |
Hardness, Brinell | 20.0 °C | 200 [-] Show Material materials with Hardness, Brinell of 200 [-] | |
Poisson's ratio | 23.0 °C | 0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-] | Typical for Malleable Cast Iron |
Shear modulus | 23.0 °C | 64 GPa Show Material materials with Shear modulus of 64 GPa | Typical for Malleable Cast Iron |
Tensile strength | 20.0 °C | 320 - 400 MPa Show Material materials with Tensile strength of 320 - 400 MPa | |
Yield strength | 20.0 °C | 170 - 210 MPa Show Material materials with Yield strength of 170 - 210 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 - 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.4E-5 1/K | Typical for Malleable Cast Iron |
Melting point | 1120 °C Show Material materials with Melting point of 1120 °C | Typical for Cast Iron | |
Specific heat capacity | 23.0 °C | 460 - 527 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 527 J/(kg·K) | Typical for Malleable Cast Iron |
Thermal conductivity | 23.0 °C | 51 W/(m·K) Show Material materials with Thermal conductivity of 51 W/(m·K) | Typical for Malleable Cast Iron |
Chemical properties
Property | Value |
---|---|
Carbon | 3 - 3.4 % Show Material materials with Carbon of 3 - 3.4 % |
Manganese | 0.4 - 0.6 % Show Material materials with Manganese of 0.4 - 0.6 % |
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % |
Sulfur | 0.12 - 0.25 % Show Material materials with Sulfur of 0.12 - 0.25 % |