EN 10025 Grade S235JR as-rolled condition (+AR)

Want to keep this datasheet? Save it now in your required format

Description

S235JR is applicated for construction parts of moderate strength load, which are not liable to inspection. Max. product thickness accounts for 25 mm. For this steel are available (see material No. 1.0120 acc. to DIN EN 10025) grades for: - folding (KQ)-S235JRC - cold forming of sections (KP)-S235JRC - cold drawing (KZ)-S235JRC

Related Standards

Equivalent Materials

Ashby charts

See where EN 10025 Grade S235JR as-rolled condition (+AR) falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

7.85 g/cm³ at 20 °C

Mechanical

Elastic modulus

E

217 GPa at -100 °C

Show Low Carbon Steel materials with Elastic modulus of 217 GPa at -100 °C

Hide chart

Elongation A80

A80

17 - 21 % at 20 °C

Show Low Carbon Steel materials with Elongation A80 of 17 - 21 % at 20 °C

Poisson's ratio

ν

0.28 [-] at 20 °C

Show Low Carbon Steel materials with Poisson's ratio of 0.28 [-] at 20 °C

Shear modulus

G

75 - 80 GPa at 20 °C

Show Low Carbon Steel materials with Shear modulus of 75 - 80 GPa at 20 °C

Typical for Carbon Steel

Tensile strength

Rm

340 - 510 MPa at 20 °C

Show Low Carbon Steel materials with Tensile strength of 340 - 510 MPa at 20 °C

Yield strength

YS

225 - 235 MPa at 20 °C

Show Low Carbon Steel materials with Yield strength of 225 - 235 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

1.08E-5 1/K at -100 °C

Unlock all property charts

Max service temperature

Tmax

500 °C

Typical for Carbon Steel

Melting point

Tm

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

cp

423 J/(kg·K) at -100 °C

Unlock all property charts

Thermal conductivity

λ

56.9 W/(m·K) at 20 °C

Unlock all property charts

Thermal diffusivity

αdiff

15.7 mm²/s at 20 °C

Unlock all property charts

Electrical

Electrical resistivity

ρel

1.83E-7 Ω·m at 20 °C

Unlock all property charts

Magnetic

Curie temperature

Tc

770 °C

Typical for Low Carbon Steel

Chemical properties

Element

Weight %

Comment

Mn

1.4 %

C

0.17 %

P

0.05 %

S

0.045 %

N

9E-3 %

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.