Property | Value | Temperature |
---|---|---|
Density | 7.85 g/cm³ Show Material materials with Density of 7.85 g/cm³ at 20.0 °C | 20.0 °C |
Mechanical
Property | Value | Temperature | Comment |
---|---|---|---|
Elastic modulus | 217 GPa Show Material materials with Elastic modulus of 217 GPa at -100.0 °C | -100.0 °C | |
212 GPa Show Material materials with Elastic modulus of 212 GPa at 20.0 °C | 20.0 °C | ||
207 GPa Show Material materials with Elastic modulus of 207 GPa at 100.0 °C | 100.0 °C | ||
199 GPa Show Material materials with Elastic modulus of 199 GPa at 200.0 °C | 200.0 °C | ||
192 GPa Show Material materials with Elastic modulus of 192 GPa at 300.0 °C | 300.0 °C | ||
184 GPa Show Material materials with Elastic modulus of 184 GPa at 400.0 °C | 400.0 °C | ||
175 GPa Show Material materials with Elastic modulus of 175 GPa at 500.0 °C | 500.0 °C | ||
164 GPa Show Material materials with Elastic modulus of 164 GPa at 600.0 °C | 600.0 °C | ||
Elongation A80 | 17 - 21 % Show Material materials with Elongation A80 of 17 - 21 % at 20.0 °C | 20.0 °C | |
Poisson's ratio | 0.28 [-] Show Material materials with Poisson's ratio of 0.28 [-] at 20.0 °C | 20.0 °C | |
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa at 23.0 °C | 23.0 °C | Typical for Low Carbon Steel |
Tensile strength | 340 - 510 MPa Show Material materials with Tensile strength of 340 - 510 MPa at 20.0 °C | 20.0 °C | |
Yield strength | 225 - 235 MPa Show Material materials with Yield strength of 225 - 235 MPa at 20.0 °C | 20.0 °C |
Thermal
Property | Value | Temperature | Comment |
---|---|---|---|
Coefficient of thermal expansion | 1.08E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.08E-5 1/K at -100.0 °C | -100.0 °C | |
1.19E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.19E-5 1/K at 20.0 °C | 20.0 °C | ||
1.25E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.25E-5 1/K at 100.0 °C | 100.0 °C | ||
1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K at 200.0 °C | 200.0 °C | ||
1.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.36E-5 1/K at 300.0 °C | 300.0 °C | ||
1.41E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.41E-5 1/K at 400.0 °C | 400.0 °C | ||
1.45E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.45E-5 1/K at 500.0 °C | 500.0 °C | ||
1.49E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.49E-5 1/K at 600.0 °C | 600.0 °C | ||
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 423 J/(kg·K) Show Material materials with Specific heat capacity of 423 J/(kg·K) at -100.0 °C | -100.0 °C | |
461 J/(kg·K) Show Material materials with Specific heat capacity of 461 J/(kg·K) at 20.0 °C | 20.0 °C | ||
479 J/(kg·K) Show Material materials with Specific heat capacity of 479 J/(kg·K) at 100.0 °C | 100.0 °C | ||
499 J/(kg·K) Show Material materials with Specific heat capacity of 499 J/(kg·K) at 200.0 °C | 200.0 °C | ||
517 J/(kg·K) Show Material materials with Specific heat capacity of 517 J/(kg·K) at 300.0 °C | 300.0 °C | ||
536 J/(kg·K) Show Material materials with Specific heat capacity of 536 J/(kg·K) at 400.0 °C | 400.0 °C | ||
558 J/(kg·K) Show Material materials with Specific heat capacity of 558 J/(kg·K) at 500.0 °C | 500.0 °C | ||
587 J/(kg·K) Show Material materials with Specific heat capacity of 587 J/(kg·K) at 600.0 °C | 600.0 °C | ||
Thermal conductivity | 56.9 W/(m·K) Show Material materials with Thermal conductivity of 56.9 W/(m·K) at 20.0 °C | 20.0 °C | |
56.4 W/(m·K) Show Material materials with Thermal conductivity of 56.4 W/(m·K) at 100.0 °C | 100.0 °C | ||
53.5 W/(m·K) Show Material materials with Thermal conductivity of 53.5 W/(m·K) at 200.0 °C | 200.0 °C | ||
49.4 W/(m·K) Show Material materials with Thermal conductivity of 49.4 W/(m·K) at 300.0 °C | 300.0 °C | ||
45.2 W/(m·K) Show Material materials with Thermal conductivity of 45.2 W/(m·K) at 400.0 °C | 400.0 °C | ||
41.3 W/(m·K) Show Material materials with Thermal conductivity of 41.3 W/(m·K) at 500.0 °C | 500.0 °C | ||
37.6 W/(m·K) Show Material materials with Thermal conductivity of 37.6 W/(m·K) at 600.0 °C | 600.0 °C | ||
Thermal diffusivity | 15.7 mm²/s Show Material materials with Thermal diffusivity of 15.7 mm²/s at 20.0 °C | 20.0 °C | |
14.5 mm²/s Show Material materials with Thermal diffusivity of 14.5 mm²/s at 100.0 °C | 100.0 °C | ||
12.9 mm²/s Show Material materials with Thermal diffusivity of 12.9 mm²/s at 200.0 °C | 200.0 °C | ||
11.2 mm²/s Show Material materials with Thermal diffusivity of 11.2 mm²/s at 300.0 °C | 300.0 °C | ||
9.6 mm²/s Show Material materials with Thermal diffusivity of 9.6 mm²/s at 400.0 °C | 400.0 °C | ||
7.9 mm²/s Show Material materials with Thermal diffusivity of 7.9 mm²/s at 500.0 °C | 500.0 °C | ||
6.3 mm²/s Show Material materials with Thermal diffusivity of 6.3 mm²/s at 600.0 °C | 600.0 °C | ||
Electrical
Property | Value | Temperature |
---|---|---|
Electrical resistivity | 1.83E-7 Ω·m Show Material materials with Electrical resistivity of 1.83E-7 Ω·m at 20.0 °C | 20.0 °C |
2.27E-7 Ω·m Show Material materials with Electrical resistivity of 2.27E-7 Ω·m at 100.0 °C | 100.0 °C | |
2.95E-7 Ω·m Show Material materials with Electrical resistivity of 2.95E-7 Ω·m at 200.0 °C | 200.0 °C | |
3.8E-7 Ω·m Show Material materials with Electrical resistivity of 3.8E-7 Ω·m at 300.0 °C | 300.0 °C | |
4.81E-7 Ω·m Show Material materials with Electrical resistivity of 4.81E-7 Ω·m at 400.0 °C | 400.0 °C | |
5.99E-7 Ω·m Show Material materials with Electrical resistivity of 5.99E-7 Ω·m at 500.0 °C | 500.0 °C | |
7.38E-7 Ω·m Show Material materials with Electrical resistivity of 7.38E-7 Ω·m at 600.0 °C | 600.0 °C | |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | ||
---|---|---|
Carbon | 0.17 % | |
Manganese | 1.4 % | |
Nitrogen | 9E-3 % | |
Phosphorus | 0.05 % | |
Sulfur | 0.045 % |