EN 10025 Grade S235JRG2C as-rolled condition (+AR)

.XLSX
.PDF
Save

Description

S235JRG2C is used for folding, section cold forming and cold drawing grades. The steel is applicable for welding constructions up to -20 °C subject to the load. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades. As a bright-steel product it is used in the form of bars, bright, straight in various conditions (see DIN EN 10277 : 1999-10).

Related Standards

Equivalent Materials

Properties

General

Density ρ

7.8 - 7.9 g/cm³ at 20 °C

Typical for Low Carbon Steel

Mechanical

Elastic modulus E

200 - 215 GPa at 20 °C

Typical for Low Carbon Steel

Elongation A

26 % at 20 °C

Elongation A80 A80

17 - 21 % at 20 °C

Elongation A80, transverse A80,trans

15 - 19 % at 20 °C

Elongation, transverse A

24 % at 20 °C

Poisson's ratio ν

0.29 [-] at 20 °C

Typical for Low Carbon Steel

Tensile strength Rm

340 - 510 MPa at 20 °C

Tensile strength, transverse Rm,trans

340 - 510 MPa at 20 °C

Yield strength YS

225 - 235 MPa at 20 °C

Yield strength, transverse YStrans

225 - 235 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

1.32E-5 - 1.38E-5 1/K at 20 °C

Typical for Low Carbon Steel

Max service temperature, long Tmaxlong

-20 - 0 °C

Melting point Tm

1480 - 1526 °C

Typical for Low Carbon Steel

Magnetic

Curie temperature Tc

770 °C

Typical for Low Carbon Steel

Chemical properties

Element

Weight %

Comment

Mn

1.4 %

C

0.17 %

P

0.05 %

S

0.05 %

N

9E-3 %

This material data has been provided by WIAM.