General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 26 % Show Material materials with Elongation of 26 % | |
Elongation A80 | 20.0 °C | 17 - 21 % Show Material materials with Elongation A80 of 17 - 21 % | |
Elongation A80, transverse | 20.0 °C | 15 - 19 % Show Material materials with Elongation A80, transverse of 15 - 19 % | |
Elongation, transverse | 20.0 °C | 24 % Show Material materials with Elongation, transverse of 24 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 340 - 510 MPa Show Material materials with Tensile strength of 340 - 510 MPa | |
Tensile strength, transverse | 20.0 °C | 340 - 510 MPa Show Material materials with Tensile strength, transverse of 340 - 510 MPa | |
Yield strength | 20.0 °C | 225 - 235 MPa Show Material materials with Yield strength of 225 - 235 MPa | |
Yield strength, transverse | 20.0 °C | 225 - 235 MPa Show Material materials with Yield strength, transverse of 225 - 235 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Max service temperature, long | -20 - 0 °C Show Material materials with Max service temperature, long of -20 - 0 °C | ||
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.17 % Show Material materials with Carbon of 0.17 % |
Manganese | 1.4 % Show Material materials with Manganese of 1.4 % |
Nitrogen | 9E-3 % Show Material materials with Nitrogen of 9E-3 % |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % |
Sulfur | 0.045 % Show Material materials with Sulfur of 0.045 % |