General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 8.8 g/cm³ Show Material materials with Density of 8.8 g/cm³ | Typical for Nickel Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Nickel Steel |
Elongation A5 | 23.0 °C | 35 % Show Material materials with Elongation A5 of 35 % | |
Hardness, Brinell | 23.0 °C | 217 [-] Show Material materials with Hardness, Brinell of 217 [-] | |
Hardness, Rockwell B | 23.0 °C | 96 [-] Show Material materials with Hardness, Rockwell B of 96 [-] | |
Hardness, Vickers | 23.0 °C | 230 [-] Show Material materials with Hardness, Vickers of 230 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Nickel Steel |
Reduction of area | 23.0 °C | 40 % Show Material materials with Reduction of area of 40 % | |
Shear modulus | 23.0 °C | 76 GPa Show Material materials with Shear modulus of 76 GPa | Typical for Nickel Steel |
Tensile strength | 23.0 °C | 520 MPa Show Material materials with Tensile strength of 520 MPa | |
Yield strength Rp0.2 | 23.0 °C | 205 MPa Show Material materials with Yield strength Rp0.2 of 205 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Melting point | 1316 - 1595 °C Show Material materials with Melting point of 1316 - 1595 °C | Typical for Nickel Steel | |
Specific heat capacity | 23.0 °C | 456 J/(kg·K) Show Material materials with Specific heat capacity of 456 J/(kg·K) | Typical for Nickel Steel |
Thermal conductivity | 23.0 °C | 10 - 50 W/(m·K) Show Material materials with Thermal conductivity of 10 - 50 W/(m·K) | Typical for Nickel Steel |
Technological properties
Property | ||
---|---|---|
Processing history | solution treated |