General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.15 g/cm³ Show Material materials with Density of 7.15 g/cm³ | Typical for Ductile (Nodular) Cast Iron |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 165 - 180 GPa Show Material materials with Elastic modulus of 165 - 180 GPa | Typical for Ductile (Nodular) Cast Iron |
Elongation A5 | 23.0 °C | 7 % Show Material materials with Elongation A5 of 7 % | |
Poisson's ratio | 23.0 °C | 0.26 - 0.31 [-] Show Material materials with Poisson's ratio of 0.26 - 0.31 [-] | Typical for Ductile (Nodular) Cast Iron |
Shear modulus | 23.0 °C | 63 - 66 GPa Show Material materials with Shear modulus of 63 - 66 GPa | Typical for Ductile (Nodular) Cast Iron |
Tensile strength | 23.0 °C | 390 MPa Show Material materials with Tensile strength of 390 MPa | |
Yield strength Rp0.2 | 23.0 °C | 210 MPa Show Material materials with Yield strength Rp0.2 of 210 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 - 1.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.6E-5 1/K | Typical for Ductile (Nodular) Cast Iron |
Melting point | 1150 - 1200 °C Show Material materials with Melting point of 1150 - 1200 °C | Typical for Ductile (Nodular) Cast Iron | |
Specific heat capacity | 23.0 °C | 460 - 502 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 502 J/(kg·K) | Typical for Ductile (Nodular) Cast Iron |
Thermal conductivity | 23.0 °C | 13 - 42 W/(m·K) Show Material materials with Thermal conductivity of 13 - 42 W/(m·K) | Typical for Ductile (Nodular) Cast Iron |