EN 10025 Grade S235J2 normalized or normalized formed (+N)

Want to keep this datasheet? Save it now in your required format

Description

The hot rolled, unalloyed quality steel S235J2 is a fine grained steel for welding constructions for alternate loading. The steel is not intended for heat treatment. Stress relieving annealing is allowed. Products in the delivery condition +N may be hot formed and/or normalized after delivery. For long products and continuous rolled flats the delivery condition is up to the producer +AR, +N or +M. The delivery condition of four-high rolled sheet is also up to the producer and may be +AR or +N. Both conditions can be ordered. For this steel are available (mat. no 1.0119, S235J2C) grades for folding, roll forming to shape and cold drawing. The steel grade S235J2 (1.0117) replaces the steel grade S235J2G3 (1.0116) according to EN 10025 (1994-03).

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.8 - 7.9 g/cm³

Show Material materials with Density of 7.8 - 7.9 g/cm³

Typical for Low Carbon Steel

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

200 - 215 GPa

Show Material materials with Elastic modulus of 200 - 215 GPa

Typical for Low Carbon Steel

Elongation

20.0 °C

21 - 26 %

Show Material materials with Elongation of 21 - 26 %

Elongation A80

20.0 °C

17 - 21 %

Show Material materials with Elongation A80 of 17 - 21 %

Elongation A80, transverse

20.0 °C

15 - 19 %

Show Material materials with Elongation A80, transverse of 15 - 19 %

Elongation, transverse

20.0 °C

21 - 24 %

Show Material materials with Elongation, transverse of 21 - 24 %

Poisson's ratio

20.0 °C

0.28 [-]

Show Material materials with Poisson's ratio of 0.28 [-]

Shear modulus

23.0 °C

82 GPa

Show Material materials with Shear modulus of 82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

330 - 510 MPa

Show Material materials with Tensile strength of 330 - 510 MPa

Yield strength

20.0 °C

165 - 235 MPa

Show Material materials with Yield strength of 165 - 235 MPa

100.0 °C

159 - 187 MPa

Show Material materials with Yield strength of 159 - 187 MPa

200.0 °C

137 - 161 MPa

Show Material materials with Yield strength of 137 - 161 MPa

250.0 °C

115 - 143 MPa

Show Material materials with Yield strength of 115 - 143 MPa

300.0 °C

102 - 122 MPa

Show Material materials with Yield strength of 102 - 122 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.32E-5 - 1.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K

Typical for Low Carbon Steel

Max service temperature

500 °C

Show Material materials with Max service temperature of 500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Show Material materials with Melting point of 1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

23.0 °C

465 J/(kg·K)

Show Material materials with Specific heat capacity of 465 J/(kg·K)

Typical for Low Carbon Steel

Thermal conductivity

23.0 °C

25 - 93 W/(m·K)

Show Material materials with Thermal conductivity of 25 - 93 W/(m·K)

Typical for Low Carbon Steel

Electrical

PropertyTemperatureValueComment

Electrical resistivity

23.0 °C

1.43E-7 - 1.74E-7 Ω·m

Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m

Typical for Carbon Steel

Magnetic

PropertyValueComment

Curie temperature

770 °C

Show Material materials with Curie temperature of 770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.17 %

Show Material materials with Carbon of 0.17 %

Copper

0.55 %

Show Material materials with Copper of 0.55 %

Manganese

1.4 %

Show Material materials with Manganese of 1.4 %

Phosphorus

0.03 %

Show Material materials with Phosphorus of 0.03 %

Sulfur

0.025 %

Show Material materials with Sulfur of 0.025 %