General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20 °C | 7.83 g/cm³ Show Material materials with Density of 7.83 g/cm³ | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | -100 °C | 217 GPa Show Material materials with Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 212 GPa Show Material materials with Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 207 GPa Show Material materials with Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
200 °C | 199 GPa Show Material materials with Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
300 °C | 192 GPa Show Material materials with Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
400 °C | 184 GPa Show Material materials with Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
500 °C | 175 GPa Show Material materials with Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
600 °C | 164 GPa Show Material materials with Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
Elongation | 17.7 % Show Material materials with Elongation of 17.7 % | Predicted Value, A200 | ||||
19.6 % Show Material materials with Elongation of 19.6 % | Predicted Value, A50 | |||||
22.3 % Show Material materials with Elongation of 22.3 % | Predicted Value, A5 | |||||
20 °C | 12 % Show Material materials with Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse | |
20 °C | 13 % Show Material materials with Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse | |
20 °C | 14 % Show Material materials with Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse | |
20 °C | 14 % Show Material materials with Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 | |
20 °C | 15 % Show Material materials with Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse | |
20 °C | 15 % Show Material materials with Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 | |
20 °C | 16 % Show Material materials with Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse | |
20 °C | 16 % Show Material materials with Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 | |
20 °C | 17 % Show Material materials with Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 | |
20 °C | 17 % Show Material materials with Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse | |
20 °C | 17 % Show Material materials with Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 18 % Show Material materials with Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 | |
20 °C | 18 % Show Material materials with Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse | |
20 °C | 18 % Show Material materials with Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 19 % Show Material materials with Elongation of 19 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse | |
20 °C | 20 % Show Material materials with Elongation of 20 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse | |
20 °C | 20 % Show Material materials with Elongation of 20 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 21 % Show Material materials with Elongation of 21 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 22 % Show Material materials with Elongation of 22 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
Hardness, Brinell | 243 [-] Show Material materials with Hardness, Brinell of 243 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel | ||||
Reduction of area | 44.0 % Show Material materials with Reduction of area of 44.0 % | Predicted Value, Transverse | ||||
52.7 % Show Material materials with Reduction of area of 52.7 % | Predicted Value | |||||
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel | ||||
Shear strength | 513.8 MPa Show Material materials with Shear strength of 513.8 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 450 - 680 MPa Show Material materials with Tensile strength of 450 - 680 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 450 - 630 MPa Show Material materials with Tensile strength of 450 - 630 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 450 - 600 MPa Show Material materials with Tensile strength of 450 - 600 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 470 - 680 MPa Show Material materials with Tensile strength of 470 - 680 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 470 - 630 MPa Show Material materials with Tensile strength of 470 - 630 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 470 - 600 MPa Show Material materials with Tensile strength of 470 - 600 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 510 - 680 MPa Show Material materials with Tensile strength of 510 - 680 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 510 - 630 MPa Show Material materials with Tensile strength of 510 - 630 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 510 - 600 MPa Show Material materials with Tensile strength of 510 - 600 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
Yield strength | 243.9 MPa Show Material materials with Yield strength of 243.9 MPa | Predicted Value, RP1 | ||||
308.5 MPa Show Material materials with Yield strength of 308.5 MPa | Predicted Value, RP1 Transverse | |||||
367.7 MPa Show Material materials with Yield strength of 367.7 MPa | Predicted Value, Transverse | |||||
379.8 MPa Show Material materials with Yield strength of 379.8 MPa | Predicted Value, RP05 | |||||
420.8 MPa Show Material materials with Yield strength of 420.8 MPa | Predicted Value, RP02 | |||||
477.7 MPa Show Material materials with Yield strength of 477.7 MPa | Predicted Value, RP02 Transverse | |||||
480.2 MPa Show Material materials with Yield strength of 480.2 MPa | Predicted Value, RP002 | |||||
20 °C | 265 MPa Show Material materials with Yield strength of 265 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 275 MPa Show Material materials with Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 285 MPa Show Material materials with Yield strength of 285 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 295 MPa Show Material materials with Yield strength of 295 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 315 MPa Show Material materials with Yield strength of 315 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 325 MPa Show Material materials with Yield strength of 325 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 335 MPa Show Material materials with Yield strength of 335 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 345 MPa Show Material materials with Yield strength of 345 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
20 °C | 355 MPa Show Material materials with Yield strength of 355 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 194 - 254 MPa Show Material materials with Yield strength of 194 - 254 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 194 - 249 MPa Show Material materials with Yield strength of 194 - 249 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 194 - 234 MPa Show Material materials with Yield strength of 194 - 234 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 194 - 224 MPa Show Material materials with Yield strength of 194 - 224 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 194 - 214 MPa Show Material materials with Yield strength of 194 - 214 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 194 MPa Show Material materials with Yield strength of 194 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 214 - 254 MPa Show Material materials with Yield strength of 214 - 254 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 214 - 249 MPa Show Material materials with Yield strength of 214 - 249 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 214 - 234 MPa Show Material materials with Yield strength of 214 - 234 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 214 - 224 MPa Show Material materials with Yield strength of 214 - 224 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 214 MPa Show Material materials with Yield strength of 214 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 224 - 254 MPa Show Material materials with Yield strength of 224 - 254 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 224 - 249 MPa Show Material materials with Yield strength of 224 - 249 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 224 - 234 MPa Show Material materials with Yield strength of 224 - 234 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 224 MPa Show Material materials with Yield strength of 224 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 234 - 254 MPa Show Material materials with Yield strength of 234 - 254 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 234 - 249 MPa Show Material materials with Yield strength of 234 - 249 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 234 MPa Show Material materials with Yield strength of 234 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 249 - 254 MPa Show Material materials with Yield strength of 249 - 254 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 249 MPa Show Material materials with Yield strength of 249 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
100 °C | 254 MPa Show Material materials with Yield strength of 254 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 166 - 226 MPa Show Material materials with Yield strength of 166 - 226 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 166 - 221 MPa Show Material materials with Yield strength of 166 - 221 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 166 - 206 MPa Show Material materials with Yield strength of 166 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 166 - 196 MPa Show Material materials with Yield strength of 166 - 196 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 166 - 186 MPa Show Material materials with Yield strength of 166 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 166 MPa Show Material materials with Yield strength of 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 186 - 226 MPa Show Material materials with Yield strength of 186 - 226 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 186 - 221 MPa Show Material materials with Yield strength of 186 - 221 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 186 - 206 MPa Show Material materials with Yield strength of 186 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 186 - 196 MPa Show Material materials with Yield strength of 186 - 196 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 186 MPa Show Material materials with Yield strength of 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 196 - 226 MPa Show Material materials with Yield strength of 196 - 226 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 196 - 221 MPa Show Material materials with Yield strength of 196 - 221 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 196 - 206 MPa Show Material materials with Yield strength of 196 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 196 MPa Show Material materials with Yield strength of 196 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 206 - 226 MPa Show Material materials with Yield strength of 206 - 226 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 206 - 221 MPa Show Material materials with Yield strength of 206 - 221 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 206 MPa Show Material materials with Yield strength of 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 221 - 226 MPa Show Material materials with Yield strength of 221 - 226 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 221 MPa Show Material materials with Yield strength of 221 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
200 °C | 226 MPa Show Material materials with Yield strength of 226 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 146 - 206 MPa Show Material materials with Yield strength of 146 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 146 - 202 MPa Show Material materials with Yield strength of 146 - 202 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 146 - 186 MPa Show Material materials with Yield strength of 146 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 146 - 176 MPa Show Material materials with Yield strength of 146 - 176 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 146 - 166 MPa Show Material materials with Yield strength of 146 - 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 146 MPa Show Material materials with Yield strength of 146 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 166 - 206 MPa Show Material materials with Yield strength of 166 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 166 - 186 MPa Show Material materials with Yield strength of 166 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 166 MPa Show Material materials with Yield strength of 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 166 - 202 MPa Show Material materials with Yield strength of 166 - 202 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 166 - 176 MPa Show Material materials with Yield strength of 166 - 176 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 176 - 206 MPa Show Material materials with Yield strength of 176 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 176 - 202 MPa Show Material materials with Yield strength of 176 - 202 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 176 - 186 MPa Show Material materials with Yield strength of 176 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 176 MPa Show Material materials with Yield strength of 176 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 186 - 206 MPa Show Material materials with Yield strength of 186 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 186 MPa Show Material materials with Yield strength of 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 186 - 202 MPa Show Material materials with Yield strength of 186 - 202 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 202 - 206 MPa Show Material materials with Yield strength of 202 - 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 202 MPa Show Material materials with Yield strength of 202 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
250 °C | 206 MPa Show Material materials with Yield strength of 206 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 126 - 186 MPa Show Material materials with Yield strength of 126 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 126 - 181 MPa Show Material materials with Yield strength of 126 - 181 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 126 - 166 MPa Show Material materials with Yield strength of 126 - 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 126 - 156 MPa Show Material materials with Yield strength of 126 - 156 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 126 - 146 MPa Show Material materials with Yield strength of 126 - 146 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 126 MPa Show Material materials with Yield strength of 126 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 146 - 186 MPa Show Material materials with Yield strength of 146 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 146 - 166 MPa Show Material materials with Yield strength of 146 - 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 146 MPa Show Material materials with Yield strength of 146 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 146 - 181 MPa Show Material materials with Yield strength of 146 - 181 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 146 - 156 MPa Show Material materials with Yield strength of 146 - 156 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 156 - 186 MPa Show Material materials with Yield strength of 156 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 156 - 181 MPa Show Material materials with Yield strength of 156 - 181 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 156 - 166 MPa Show Material materials with Yield strength of 156 - 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 156 MPa Show Material materials with Yield strength of 156 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 166 - 186 MPa Show Material materials with Yield strength of 166 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 166 MPa Show Material materials with Yield strength of 166 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 166 - 181 MPa Show Material materials with Yield strength of 166 - 181 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 181 - 186 MPa Show Material materials with Yield strength of 181 - 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 181 MPa Show Material materials with Yield strength of 181 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | |||
300 °C | 186 MPa Show Material materials with Yield strength of 186 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | -100 °C | 1.08e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 1.19e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 1.25e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
200 °C | 1.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
300 °C | 1.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
400 °C | 1.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
500 °C | 1.45e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
600 °C | 1.49e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
Max service temperature | 305.4 °C Show Material materials with Max service temperature of 305.4 °C | Predicted Value, Long | ||||
500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |||||
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel | ||||
Specific heat capacity | -100 °C | 423 J/(kg·K) Show Material materials with Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 461 J/(kg·K) Show Material materials with Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 479 J/(kg·K) Show Material materials with Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
200 °C | 499 J/(kg·K) Show Material materials with Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
300 °C | 517 J/(kg·K) Show Material materials with Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
400 °C | 536 J/(kg·K) Show Material materials with Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
500 °C | 558 J/(kg·K) Show Material materials with Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
600 °C | 587 J/(kg·K) Show Material materials with Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
Thermal conductivity | -100 °C | 37.6 W/(m·K) Show Material materials with Thermal conductivity of 37.6 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 42.2 W/(m·K) Show Material materials with Thermal conductivity of 42.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 43.2 W/(m·K) Show Material materials with Thermal conductivity of 43.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
200 °C | 42.9 W/(m·K) Show Material materials with Thermal conductivity of 42.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
300 °C | 41.2 W/(m·K) Show Material materials with Thermal conductivity of 41.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
400 °C | 39.1 W/(m·K) Show Material materials with Thermal conductivity of 39.1 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
500 °C | 36.6 W/(m·K) Show Material materials with Thermal conductivity of 36.6 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
600 °C | 34.1 W/(m·K) Show Material materials with Thermal conductivity of 34.1 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
Thermal diffusivity | -100 °C | 12.9 mm²/s Show Material materials with Thermal diffusivity of 12.9 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 11.7 mm²/s Show Material materials with Thermal diffusivity of 11.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 11.2 mm²/s Show Material materials with Thermal diffusivity of 11.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
200 °C | 10.3 mm²/s Show Material materials with Thermal diffusivity of 10.3 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
300 °C | 9.4 mm²/s Show Material materials with Thermal diffusivity of 9.4 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
400 °C | 8.3 mm²/s Show Material materials with Thermal diffusivity of 8.3 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
500 °C | 7.1 mm²/s Show Material materials with Thermal diffusivity of 7.1 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
600 °C | 5.7 mm²/s Show Material materials with Thermal diffusivity of 5.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Electrical conductivity | 7 S/m Show Material materials with Electrical conductivity of 7 S/m | Predicted Value | ||||
Electrical resistivity | -100 °C | 1.82e-07 Ω·m Show Material materials with Electrical resistivity of 1.82e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | |
20 °C | 2.47e-07 Ω·m Show Material materials with Electrical resistivity of 2.47e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
100 °C | 2.96e-07 Ω·m Show Material materials with Electrical resistivity of 2.96e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
200 °C | 3.68e-07 Ω·m Show Material materials with Electrical resistivity of 3.68e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
300 °C | 4.55e-07 Ω·m Show Material materials with Electrical resistivity of 4.55e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
400 °C | 5.56e-07 Ω·m Show Material materials with Electrical resistivity of 5.56e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
500 °C | 6.75e-07 Ω·m Show Material materials with Electrical resistivity of 6.75e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | ||
600 °C | 8.13e-07 Ω·m Show Material materials with Electrical resistivity of 8.13e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Carbon | 0.2 % Show Material materials with Carbon of 0.2 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Copper | 0.55 % Show Material materials with Copper of 0.55 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Manganese | 1.6 % Show Material materials with Manganese of 1.6 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Phosphorus | 0.025 % Show Material materials with Phosphorus of 0.025 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Silicon | 0.55 % Show Material materials with Silicon of 0.55 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Sulfur | 0.025 % Show Material materials with Sulfur of 0.025 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |