EN 1652 Grade Cu-ETP R240

View suppliers (36)
Want to keep this datasheet? Save it now in your required format

Description

Cu-ETP, mat. No CW004A, is an oxygenous copper with Cu >= 99,9%. To the comparable DIN-mark E-Cu58, mat. No 2.0065 acc. to DIN 1787 : 1973-01 applies: The most excellent material property is its high thermal and electrical conductivity. Tensile strength and Brinell hardness are increasable by cold forming. The material does not show any embrittlement at low temperatures and has a high corrosion resistance particularly to drinking and industrial water. It is not hydrogen resistant. Processing properties: hot forming: very good cold forming: very good machinability: unfavorable hard soldering: good soft soldering: very good gas-shielded welding: moderately burnishing: very good Application: Due to the very high conductivity use in electrical engineering, electronics application. Furthermore in food and beverage industry, refrigeration and air-condition technology, in machine, ship, apparatus and vehicle engineering, in household as well as for hardware, in handcraft and in construction trade. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.9 - 8.94 g/cm³

Show Material materials with Density of 8.9 - 8.94 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

127 GPa

Show Material materials with Elastic modulus of 127 GPa

Elongation

20.0 °C

15 %

Show Material materials with Elongation of 15 %

Elongation A50

20.0 °C

8 %

Show Material materials with Elongation A50 of 8 %

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

23.0 °C

48 GPa

Show Material materials with Shear modulus of 48 GPa

Typical for Wrought Copper Pure / Low Alloyed Copper

Tensile strength

20.0 °C

240 - 300 MPa

Show Material materials with Tensile strength of 240 - 300 MPa

Yield strength Rp0.2

20.0 °C

160 - 180 MPa

Show Material materials with Yield strength Rp0.2 of 160 - 180 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.68E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.68E-5 1/K

200.0 °C

1.73E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.73E-5 1/K

300.0 °C

1.77E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K

Melting point

965 - 1100 °C

Show Material materials with Melting point of 965 - 1100 °C

Typical for Wrought Copper Pure / Low Alloyed Copper

Specific heat capacity

-150.0 °C

282 J/(kg·K)

Show Material materials with Specific heat capacity of 282 J/(kg·K)

-50.0 °C

361 J/(kg·K)

Show Material materials with Specific heat capacity of 361 J/(kg·K)

20.0 °C

386 J/(kg·K)

Show Material materials with Specific heat capacity of 386 J/(kg·K)

Unlock all property charts

Thermal conductivity

-253.0 °C

1298 W/(m·K)

Show Material materials with Thermal conductivity of 1298 W/(m·K)

-200.0 °C

574 W/(m·K)

Show Material materials with Thermal conductivity of 574 W/(m·K)

-100.0 °C

435 W/(m·K)

Show Material materials with Thermal conductivity of 435 W/(m·K)

20.0 °C

390 - 394 W/(m·K)

Show Material materials with Thermal conductivity of 390 - 394 W/(m·K)

100.0 °C

385 W/(m·K)

Show Material materials with Thermal conductivity of 385 W/(m·K)

200.0 °C

381 W/(m·K)

Show Material materials with Thermal conductivity of 381 W/(m·K)

300.0 °C

377 W/(m·K)

Show Material materials with Thermal conductivity of 377 W/(m·K)

Unlock all property charts

Chemical properties

PropertyValue

Bismuth

5E-4 %

Show Material materials with Bismuth of 5E-4 %

Copper

99.9 %

Show Material materials with Copper of 99.9 %

Lead

5E-3 %

Show Material materials with Lead of 5E-3 %

Oxygen

0.04 %

Show Material materials with Oxygen of 0.04 %