EN 12163 Grade CuZn23Al6Mn4Fe3Pb R780

View suppliers (1)
Want to keep this datasheet? Save it now in your required format

Description

CuZn23Al6Mn4Fe3Pb (CW 704R former identification: CuZn23Al6Mn4Fe3) is an unhardenable copper alloy. High hardness and strength values are achievable by cold forming only. Strength properties are improved by AL- and Fe- addition. Manganese and aluminium increase corrosion resistance. The alloy is seawater resistant. Processing properties: warm forming: good cold forming: unfavorable machinability: good hard soldering: unfavorable soft soldering: unfavorable burnishing: very good CuZn23Al6Mn4Fe3Pb is a construction material of very high strength, particularly for high static loading. Application for plates and tubes in condensators and heat-exchangers as well as for seawater pipes.

Related Standards

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.2 g/cm³

Show Material materials with Density of 8.2 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

105 GPa

Show Material materials with Elastic modulus of 105 GPa

Elongation

20.0 °C

8 %

Show Material materials with Elongation of 8 %

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

780 MPa

Show Material materials with Tensile strength of 780 MPa

Yield strength Rp0.2

20.0 °C

540 MPa

Show Material materials with Yield strength Rp0.2 of 540 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

20.0 °C

27 W/(m·K)

Show Material materials with Thermal conductivity of 27 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

4.00E+6 S/m

Show Material materials with Electrical conductivity of 4.00E+6 S/m

Specific Electrical conductivity

6.9 % IACS

Show Material materials with Specific Electrical conductivity of 6.9 % IACS

Chemical properties

PropertyValue

Aluminium

5 - 7 %

Show Material materials with Aluminium of 5 - 7 %

Copper

63 - 65.5 %

Show Material materials with Copper of 63 - 65.5 %

Iron

2 - 3.5 %

Show Material materials with Iron of 2 - 3.5 %

Lead

1 %

Show Material materials with Lead of 1 %

Manganese

3.5 - 5 %

Show Material materials with Manganese of 3.5 - 5 %

Nickel

0.5 %

Show Material materials with Nickel of 0.5 %