EN 12167 Grade CuNi18Zn20 H150

View suppliers (7)
Want to keep this datasheet? Save it now in your required format


Material CuNi18Zn20, mat. No. CW409J is an alloy of high strength and hardness. To the comparabel mark CuNi18Zn20, mat. No. 2.0740, acc. to DIN 17663 : 1983-12 applies: Strength is further increasable due to the high strain hardening capability. The material does not embrittle at low temperatures. Low electrical and thermal conductivity. The alloy is non-magnetic, corrosion resistance is better than for pure copper. Processing properties: warm forming: moderately cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: very good burnishing: very good Application: In electrical engineering and electronics for springs, contacts, membranes as well as in precision engineering and in equipment manufacturing. In food industry, for musical instruments, glasses frames, safety keys as well as in construction trade for paneling, show-cases and stairrails.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

8.4 - 8.9 g/cm³

Show Material materials with Density of 8.4 - 8.9 g/cm³

Typical for Wrought Copper Nickel Silver Grade



Elastic modulus

23.0 °C

120 - 140 GPa

Show Material materials with Elastic modulus of 120 - 140 GPa

Typical for Wrought Copper Nickel Silver Grade

Hardness, Brinell

20.0 °C

150 [-]

Show Material materials with Hardness, Brinell of 150 [-]

Hardness, Vickers

20.0 °C

155 [-]

Show Material materials with Hardness, Vickers of 155 [-]

Poisson's ratio

23.0 °C

0.32 [-]

Show Material materials with Poisson's ratio of 0.32 [-]

Typical for Wrought Copper Nickel Silver Grade



Coefficient of thermal expansion

23.0 °C

1.6E-5 - 1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.9E-5 1/K

Typical for Wrought Copper Nickel Silver Grade

Melting point

875 - 1135 °C

Show Material materials with Melting point of 875 - 1135 °C

Typical for Wrought Copper Nickel Silver Grade

Specific heat capacity

23.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Typical for Wrought Copper Nickel Silver Grade

Thermal conductivity

23.0 °C

21 - 116 W/(m·K)

Show Material materials with Thermal conductivity of 21 - 116 W/(m·K)

Typical for Wrought Copper Nickel Silver Grade

Chemical properties



60 - 63 %

Show Material materials with Copper of 60 - 63 %


0.3 %

Show Material materials with Iron of 0.3 %


0.03 %

Show Material materials with Lead of 0.03 %


0.5 %

Show Material materials with Manganese of 0.5 %


17 - 19 %

Show Material materials with Nickel of 17 - 19 %


0.03 %

Show Material materials with Tin of 0.03 %