EN 12166 Grade CuZn15 H01

Want to keep this datasheet? Save it now in your required format

Description

CuZn15 (CW502L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn10. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn15 is used in electrical engineering, for metal goods as well as in jewelry industry, for metall hoses, pressure measuring instruments, signs, casings and suspension bodies. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

100 - 125 GPa

Show Material materials with Elastic modulus of 100 - 125 GPa

Typical for Wrought Copper Brass

Elongation

20.0 °C

20 %

Show Material materials with Elongation of 20 %

Elongation A10

20.0 °C

18 %

Show Material materials with Elongation A10 of 18 %

Elongation A100

20.0 °C

10 - 14 %

Show Material materials with Elongation A100 of 10 - 14 %

Hardness, Vickers

20.0 °C

115 - 150 [-]

Show Material materials with Hardness, Vickers of 115 - 150 [-]

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

360 - 500 MPa

Show Material materials with Tensile strength of 360 - 500 MPa

Yield strength Rp0.2

20.0 °C

250 - 270 MPa

Show Material materials with Yield strength Rp0.2 of 250 - 270 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

23.0 °C

371 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K)

Typical for Wrought Copper Brass

Thermal conductivity

23.0 °C

100 - 234 W/(m·K)

Show Material materials with Thermal conductivity of 100 - 234 W/(m·K)

Typical for Wrought Copper Brass

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Copper

84 - 86 %

Show Material materials with Copper of 84 - 86 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %