General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.67 g/cm³ Show Material materials with Density of 8.67 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 119 GPa Show Material materials with Elastic modulus of 119 GPa | |
Hardness, Brinell | 20.0 °C | 110 [-] Show Material materials with Hardness, Brinell of 110 [-] | |
Hardness, Vickers | 20.0 °C | 115 [-] Show Material materials with Hardness, Vickers of 115 [-] | |
Poisson's ratio | 20.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Shear modulus | 23.0 °C | 40 GPa Show Material materials with Shear modulus of 40 GPa | Typical for Wrought Copper Brass |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 380 J/(kg·K) Show Material materials with Specific heat capacity of 380 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 142 W/(m·K) Show Material materials with Thermal conductivity of 142 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.90E+7 S/m Show Material materials with Electrical conductivity of 1.90E+7 S/m |
Specific Electrical conductivity | 33 % IACS Show Material materials with Specific Electrical conductivity of 33 % IACS |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Copper | 79 - 81 % Show Material materials with Copper of 79 - 81 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Tin | 0.1 % Show Material materials with Tin of 0.1 % |