EN 12168 Grade CuZn35Pb2 H110

.XLSX
.PDF
Save

Description

Material CuZn35Pb2, mat. No. CW601N, is an unhardenable wrought alloy. To the comparable make CuZn36Pb1,5, mat. No. 2.0331 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: good cold forming: good machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Wheels for circuit boards in watch industry, matrices for printing industry, clamps for electrical engineering, nipples, screws.

Related standards

Equivalent Materials

Properties

General

Density ρ

8.5 g/cm³ at 20 °C

Material Information

Dimension

0.0-10.0

Mechanical

Hardness, Brinell HB

110 - 160 [-] at 20 °C

Hardness, Vickers HV

120 - 170 [-] at 20 °C

Tensile strength Rm

440 MPa at 20 °C

Yield strength Rp0.2 Rp0.2

340 MPa at 20 °C

Chemical properties

Element

Weight %

Comment

Cu

62 - 63.5 %

Pb

1.6 - 2.5 %

Ni

0.3 %

Fe

0.1 %

Sn

0.1 %

More

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Find a supplier

We can help you find a supplier of EN 12168 Grade CuZn35Pb2 H110

We will evaluate your request and get back to you soon.