Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.78 g/cm³ Show Material materials with Density of 2.78 g/cm³ | T361 | AA Standards, ASTM B209 |
3.0 g/cm³ Show Material materials with Density of 3.0 g/cm³ | T361 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T361 | AA Standards, ASTM B209 | |
Elongation | 8.0 % Show Material materials with Elongation of 8.0 % | T361 | AA Standards, ASTM B209 | A50 |
9.0 % Show Material materials with Elongation of 9.0 % | T361 | AA Standards, ASTM B209 | A50 | |
9.0 % Show Material materials with Elongation of 9.0 % | T361 | AA Standards, ASTM B209 | A100 | |
12.0 % Show Material materials with Elongation of 12.0 % | T361 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 455.0 MPa Show Material materials with Tensile strength of 455.0 MPa | T361 | AA Standards, ASTM B209 | |
460.0 MPa Show Material materials with Tensile strength of 460.0 MPa | T361 | AA Standards, ASTM B209 | ||
470.0 MPa Show Material materials with Tensile strength of 470.0 MPa | T361 | AA Standards, ASTM B209 | ||
510.0 MPa Show Material materials with Tensile strength of 510.0 MPa | T361 | |||
Yield strength | 340.0 MPa Show Material materials with Yield strength of 340.0 MPa | T361 | AA Standards, ASTM B209 | RP02 |
345.0 MPa Show Material materials with Yield strength of 345.0 MPa | T361 | AA Standards, ASTM B209 | RP02 | |
350.0 MPa Show Material materials with Yield strength of 350.0 MPa | T361 | AA Standards, ASTM B209 | RP02 | |
390.0 MPa Show Material materials with Yield strength of 390.0 MPa | T361 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T361 | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | T361 | AA Standards, ASTM B209 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | T361 | AA Standards, ASTM B209 | |
Melting point | 500.0 °C Show Material materials with Melting point of 500.0 °C | T361 | ||
505.0 - 635.0 °C Show Material materials with Melting point of 505.0 - 635.0 °C | T361 | AA Standards, ASTM B209 | ||
Specific heat capacity | 870.0 J/(kg·K) Show Material materials with Specific heat capacity of 870.0 J/(kg·K) | T361 | ||
Thermal conductivity | 120.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 W/(m·K) | T361 | ||
121.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 121.0 - 193.0 W/(m·K) | T361 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 17000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 17000000.0 - 29000000.0 S/m | T361 | AA Standards, ASTM B209 | |
17000000 S/m Show Material materials with Electrical conductivity of 17000000 S/m | T361 | Typical/derived value | ||
Electrical resistivity | 3.45e-08 - 5.88e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 5.88e-08 Ω·m | T361 | AA Standards, ASTM B209 | |
5.8999999999999986e-08 Ω·m Show Material materials with Electrical resistivity of 5.8999999999999986e-08 Ω·m | T361 | Typical value | ||
Specific Electrical conductivity | 30.0 % IACS Show Material materials with Specific Electrical conductivity of 30.0 % IACS | T361 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 90.7 - 94.7 % Show Material materials with Aluminium of 90.7 - 94.7 % | T361 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T361 | AA Standards, ASTM B209 |
Copper | 3.8 - 4.9 % Show Material materials with Copper of 3.8 - 4.9 % | T361 | AA Standards, ASTM B209 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T361 | AA Standards, ASTM B209 |
0.5 % Show Material materials with Iron of 0.5 % | T361 | ||
Magnesium | 1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 % | T361 | AA Standards, ASTM B209 |
Manganese | 0.3 - 0.9 % Show Material materials with Manganese of 0.3 - 0.9 % | T361 | AA Standards, ASTM B209 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T361 | |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | T361 | AA Standards, ASTM B209 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T361 | AA Standards, ASTM B209 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T361 | AA Standards, ASTM B209 |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % | T361 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T4,T3, T351, T3510, T3511), d (T6, T861, T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T4, T3, T351, T3510, T3511, T6), not suitable (T361, T861, T81, T851, T8510, T8511) | |