General
Property | Value | Condition |
---|---|---|
Density | 4.4 g/cm³ Show Material materials with Density of 4.4 g/cm³ | Transformed-Beta |
Mechanical
Property | Value | Condition |
---|---|---|
Elastic modulus | 110.0 GPa Show Material materials with Elastic modulus of 110.0 GPa | Transformed-Beta |
Elongation | 6.9 % Show Material materials with Elongation of 6.9 % | Transformed-Beta |
Tensile strength | 950.0 MPa Show Material materials with Tensile strength of 950.0 MPa | Transformed-Beta |
Yield strength | 870.0 MPa Show Material materials with Yield strength of 870.0 MPa | Transformed-Beta |
Thermal
Property | Value | Condition | Comment |
---|---|---|---|
Coefficient of thermal expansion | 9.4e-06 1/K Show Material materials with Coefficient of thermal expansion of 9.4e-06 1/K | Transformed-Beta | |
Melting point | 1500.0 - 1750.0 °C Show Material materials with Melting point of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy | |
Specific heat capacity | 560.0 J/(kg·K) Show Material materials with Specific heat capacity of 560.0 J/(kg·K) | Transformed-Beta | |
Thermal conductivity | 7.1 W/(m·K) Show Material materials with Thermal conductivity of 7.1 W/(m·K) | Transformed-Beta |
Chemical properties
Property | Value | Condition |
---|---|---|
Aluminium | 5.5 - 6.5 % Show Material materials with Aluminium of 5.5 - 6.5 % | Transformed-Beta |
Carbon | 0.08 % Show Material materials with Carbon of 0.08 % | Transformed-Beta |
Hydrogen | 0.013 % Show Material materials with Hydrogen of 0.013 % | Transformed-Beta |
Iron | 0.25 % Show Material materials with Iron of 0.25 % | Transformed-Beta |
Nitrogen | 0.03 % Show Material materials with Nitrogen of 0.03 % | Transformed-Beta |
Other | 0.4 % Show Material materials with Other of 0.4 % | Transformed-Beta |
Oxygen | 0.13 % Show Material materials with Oxygen of 0.13 % | Transformed-Beta |
Titanium | 88.1 - 91.0 % Show Material materials with Titanium of 88.1 - 91.0 % | Transformed-Beta |
Vanadium | 3.5 - 4.5 % Show Material materials with Vanadium of 3.5 - 4.5 % | Transformed-Beta |