AA 2219 T8

Want to keep this datasheet? Save it now in your required format

Description

Aluminum Alloy AA 2219, an age-hardenable alloy is produced with a copper additive. It is well-known for its excellent structural strength and it’s used for numerous high temperature applications. It is a suitable alloy for many metalworking processes including machining, forming, heat treatment, cold working, and more.

Equivalent Materials

This material data has been provided by MakeItFrom.com.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueCondition

Density

3.1 g/cm³

Show Material materials with Density of 3.1 g/cm³

T8

Mechanical

PropertyValueConditionComment

Elastic modulus

74.0 GPa

Show Material materials with Elastic modulus of 74.0 GPa

T8

Unlock all property charts

Elongation

9.0 %

Show Material materials with Elongation of 9.0 %

T8

Unlock all property charts

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Shear modulus

26.0 - 27.5 GPa

Show Material materials with Shear modulus of 26.0 - 27.5 GPa

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Tensile strength

450.0 MPa

Show Material materials with Tensile strength of 450.0 MPa

T8

Unlock all property charts

Yield strength

340.0 MPa

Show Material materials with Yield strength of 340.0 MPa

T8

Unlock all property charts

Thermal

PropertyValueCondition

Coefficient of thermal expansion

2.2e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.2e-05 1/K

T8

Unlock all property charts

Melting point

540.0 °C

Show Material materials with Melting point of 540.0 °C

T8

Specific heat capacity

860.0 J/(kg·K)

Show Material materials with Specific heat capacity of 860.0 J/(kg·K)

T8

Unlock all property charts

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

T8

Unlock all property charts

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 30000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 30000000.0 S/m

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Electrical resistivity

3.4e-08 - 6e-08 Ω·m

Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Chemical properties

PropertyValueCondition

Aluminium

91.5 - 93.8 %

Show Material materials with Aluminium of 91.5 - 93.8 %

T8

Copper

5.8 - 6.8 %

Show Material materials with Copper of 5.8 - 6.8 %

T8

Iron

0.3 %

Show Material materials with Iron of 0.3 %

T8

Magnesium

0.02 %

Show Material materials with Magnesium of 0.02 %

T8

Manganese

0.2 - 0.4 %

Show Material materials with Manganese of 0.2 - 0.4 %

T8

Other

0.15 %

Show Material materials with Other of 0.15 %

T8

Silicon

0.2 %

Show Material materials with Silicon of 0.2 %

T8

Titanium

0.02 - 0.1 %

Show Material materials with Titanium of 0.02 - 0.1 %

T8

Vanadium

0.05 - 0.15 %

Show Material materials with Vanadium of 0.05 - 0.15 %

T8

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

T8

Zirconium

0.1 - 0.25 %

Show Material materials with Zirconium of 0.1 - 0.25 %

T8

Technological properties

Property
Workability

Moderate Workability