Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.84 g/cm³ Show Material materials with Density of 2.84 g/cm³ | T87 | AA Standards, ASTM B209 |
2.84 g/cm³ Show Material materials with Density of 2.84 g/cm³ | T87 | ||
3.1 g/cm³ Show Material materials with Density of 3.1 g/cm³ | T87 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | T87 | AA Standards | ||
Creep strength | 24 °C | 420 MPa Show Material materials with Creep strength of 420 MPa | T87 | up to 1000 hours | |
100 °C | 315 MPa Show Material materials with Creep strength of 315 MPa | T87 | up to 1000 hours | ||
150 °C | 235 MPa Show Material materials with Creep strength of 235 MPa | T87 | up to 1000 hours | ||
205 °C | 150 MPa Show Material materials with Creep strength of 150 MPa | T87 | up to 1000 hours | ||
230 °C | 130 MPa Show Material materials with Creep strength of 130 MPa | T87 | up to 1000 hours | ||
260 °C | 105 MPa Show Material materials with Creep strength of 105 MPa | T87 | up to 1000 hours | ||
270 °C | 17 MPa Show Material materials with Creep strength of 17 MPa | T87 | up to 1000 hours | ||
315 °C | 34 MPa Show Material materials with Creep strength of 34 MPa | T87 | up to 1000 hours | ||
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T87 | AA Standards, ASTM B209 | ||
73 GPa Show Material materials with Elastic modulus of 73 GPa | T87 | ||||
74.0 GPa Show Material materials with Elastic modulus of 74.0 GPa | T87 | ||||
Elongation | 2.0 % Show Material materials with Elongation of 2.0 % | T87 | AA Standards, ASTM B209 | A100 | |
3.0 % Show Material materials with Elongation of 3.0 % | T87 | AA Standards, ASTM B209 | A100 | ||
5.0 % Show Material materials with Elongation of 5.0 % | T87 | AA Standards, ASTM B209 | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | T87 | AA Standards, ASTM B209 | A100 | ||
6.0 % Show Material materials with Elongation of 6.0 % | T87 | AA Standards, ASTM B209 | A50 | ||
6.0 % Show Material materials with Elongation of 6.0 % | T87 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Elongation of 7.0 % | T87 | AA Standards, ASTM B209 | A50 | ||
7.4 % Show Material materials with Elongation of 7.4 % | T87 | ||||
10.0 % Show Material materials with Elongation of 10.0 % | T87 | AA Standards | A50 | ||
10 % Show Material materials with Elongation of 10 % | T87 | ||||
Fatigue strength | 103 MPa Show Material materials with Fatigue strength of 103 MPa | T87 | for 5x10⁸ cycles | ||
Plane-Strain Fracture Toughnes | -196 °C | 38.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 38.9 MPa·√m | T87 | For plate in T-L direction | |
24 °C | 30.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 30.8 MPa·√m | T87 | For plate in T-L direction | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 GPa Show Material materials with Shear modulus of 26.0 GPa | T87 | |||
Tensile strength | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T87 | AA Standards, ASTM B209 | ||
425.0 MPa Show Material materials with Tensile strength of 425.0 MPa | T87 | AA Standards, ASTM B209 | |||
440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T87 | AA Standards, ASTM B209 | |||
475.0 MPa Show Material materials with Tensile strength of 475.0 MPa | T87 | AA Standards | |||
475 MPa Show Material materials with Tensile strength of 475 MPa | T87 | ||||
480.0 MPa Show Material materials with Tensile strength of 480.0 MPa | T87 | ||||
Yield strength | 340.0 MPa Show Material materials with Yield strength of 340.0 MPa | T87 | AA Standards, ASTM B209 | RP02 | |
345.0 MPa Show Material materials with Yield strength of 345.0 MPa | T87 | AA Standards, ASTM B209 | RP02 | ||
350.0 MPa Show Material materials with Yield strength of 350.0 MPa | T87 | AA Standards, ASTM B209 | RP02 | ||
360.0 MPa Show Material materials with Yield strength of 360.0 MPa | T87 | AA Standards, ASTM B209 | RP02 | ||
395.0 MPa Show Material materials with Yield strength of 395.0 MPa | T87 | AA Standards | RP02 | ||
395 MPa Show Material materials with Yield strength of 395 MPa | T87 | RP02 | |||
400.0 MPa Show Material materials with Yield strength of 400.0 MPa | T87 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.2e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 1/K | T87 | ||
20 °C | 2.23e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.23e-05 1/K | T87 | AA Standards, ASTM B209 | |
100 °C | 2.23e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.23e-05 1/K | T87 | AA Standards, ASTM B209 | |
Melting point | 540.0 °C Show Material materials with Melting point of 540.0 °C | T87 | ||
545.0 - 645.0 °C Show Material materials with Melting point of 545.0 - 645.0 °C | T87 | AA Standards, ASTM B209 | ||
Specific heat capacity | 860.0 J/(kg·K) Show Material materials with Specific heat capacity of 860.0 J/(kg·K) | T87 | ||
Thermal conductivity | 113.0 - 172.0 W/(m·K) Show Material materials with Thermal conductivity of 113.0 - 172.0 W/(m·K) | T87 | AA Standards, ASTM B209 | |
120.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 W/(m·K) | T87 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 16000000.0 - 26000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 26000000.0 S/m | T87 | AA Standards, ASTM B209 | |
17000000 S/m Show Material materials with Electrical conductivity of 17000000 S/m | T87 | Typical/derived value | ||
Electrical resistivity | 3.85e-08 - 6.25e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 - 6.25e-08 Ω·m | T87 | AA Standards, ASTM B209 | |
5.7e-08 Ω·m Show Material materials with Electrical resistivity of 5.7e-08 Ω·m | T87 | Typical value | ||
Specific Electrical conductivity | 30.0 % IACS Show Material materials with Specific Electrical conductivity of 30.0 % IACS | T87 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 91.5 - 93.8 % Show Material materials with Aluminium of 91.5 - 93.8 % | T87 | |
Copper | 5.8 - 6.8 % Show Material materials with Copper of 5.8 - 6.8 % | T87 | AA Standards, ASTM B209 |
Iron | 0.30 % Show Material materials with Iron of 0.30 % | T87 | AA Standards, ASTM B209 |
0.3 % Show Material materials with Iron of 0.3 % | T87 | ||
Magnesium | 0.02 % Show Material materials with Magnesium of 0.02 % | T87 | AA Standards, ASTM B209 |
Manganese | 0.2 - 0.4 % Show Material materials with Manganese of 0.2 - 0.4 % | T87 | AA Standards, ASTM B209 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T87 | |
Silicon | 0.2 % Show Material materials with Silicon of 0.2 % | T87 | AA Standards, ASTM B209 |
Titanium | 0.02 - 0.1 % Show Material materials with Titanium of 0.02 - 0.1 % | T87 | AA Standards, ASTM B209 |
Vanadium | 0.05 - 0.15 % Show Material materials with Vanadium of 0.05 - 0.15 % | T87 | AA Standards, ASTM B209 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T87 | AA Standards, ASTM B209 |
Zirconium | 0.1 - 0.25 % Show Material materials with Zirconium of 0.1 - 0.25 % | T87 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87) | |