Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³ | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 |
2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³ | H18 | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H18 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 70.0 MPa Show Material materials with Bending Fatigue Strength of 70.0 MPa | H18 | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa | H18 | ||||
Elongation | -195 °C | 23 % Show Material materials with Elongation of 23 % | H18 | Elongation in 50 mm | |
-80 °C | 11 % Show Material materials with Elongation of 11 % | H18 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongation of 1.0 % | H18 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongation of 2.0 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B313 | A50 | ||
3.0 % Show Material materials with Elongation of 3.0 % | H18 | AA Standards, ASTM B210 | A50 | ||
4.0 % Show Material materials with Elongation of 4.0 % | H18 | AA Standards, ASTM B209, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | A50 | ||
4.0 % Show Material materials with Elongation of 4.0 % | H18 | AA Standards, ASTM B345 | A100 | ||
4.6 % Show Material materials with Elongation of 4.6 % | H18 | ||||
9.0 % Show Material materials with Elongation of 9.0 % | H18 | AA Standards | A100 | ||
0 °C | 10 % Show Material materials with Elongation of 10 % | H18 | Elongation in 50 mm | ||
24 °C | 10 % Show Material materials with Elongation of 10 % | H18 | Elongation in 50 mm | ||
100 °C | 10 % Show Material materials with Elongation of 10 % | H18 | Elongation in 50 mm | ||
150 °C | 11 % Show Material materials with Elongation of 11 % | H18 | Elongation in 50 mm | ||
205 °C | 18 % Show Material materials with Elongation of 18 % | H18 | Elongation in 50 mm | ||
260 °C | 60 % Show Material materials with Elongation of 60 % | H18 | Elongation in 50 mm | ||
315 °C | 70 % Show Material materials with Elongation of 70 % | H18 | Elongation in 50 mm | ||
370 °C | 70 % Show Material materials with Elongation of 70 % | H18 | Elongation in 50 mm | ||
Fatigue strength | 69 MPa Show Material materials with Fatigue strength of 69 MPa | H18 | for 5x10⁸ cycles | ||
Hardness, Brinell | 55.0 [-] Show Material materials with Hardness, Brinell of 55.0 [-] | H18 | AA Standards | ||
55.0 [-] Show Material materials with Hardness, Brinell of 55.0 [-] | H18 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H18 | |||
Shear strength | 110.0 MPa Show Material materials with Shear strength of 110.0 MPa | H18 | |||
Tensile strength | -195 °C | 283 MPa Show Material materials with Tensile strength of 283 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 220 MPa Show Material materials with Tensile strength of 220 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
185.0 MPa Show Material materials with Tensile strength of 185.0 MPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |||
200.0 MPa Show Material materials with Tensile strength of 200.0 MPa | H18 | AA Standards | |||
0 °C | 207 MPa Show Material materials with Tensile strength of 207 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | H18 | ||||
24 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Tensile strength of 97 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 28 MPa Show Material materials with Tensile strength of 28 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 19 MPa Show Material materials with Tensile strength of 19 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -200 °C | 230 MPa Show Material materials with Yield strength of 230 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 210 MPa Show Material materials with Yield strength of 210 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 190 MPa Show Material materials with Yield strength of 190 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
165.0 MPa Show Material materials with Yield strength of 165.0 MPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | RP02 | ||
185.0 MPa Show Material materials with Yield strength of 185.0 MPa | H18 | AA Standards | RP02 | ||
190.0 MPa Show Material materials with Yield strength of 190.0 MPa | H18 | ||||
25 °C | 185 MPa Show Material materials with Yield strength of 185 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 145 MPa Show Material materials with Yield strength of 145 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 17 MPa Show Material materials with Yield strength of 17 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 12 MPa Show Material materials with Yield strength of 12 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | H18 | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
Melting point | 640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
640.0 °C Show Material materials with Melting point of 640.0 °C | H18 | |||
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | H18 | ||
Thermal conductivity | 159.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 159.0 - 193.0 W/(m·K) | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
180.0 W/(m·K) Show Material materials with Thermal conductivity of 180.0 W/(m·K) | H18 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 23000000 S/m Show Material materials with Electrical conductivity of 23000000 S/m | H18 | Typical value | |
24000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 - 29000000.0 S/m | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | ||
Electrical resistivity | 3.45e-08 - 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 4.17e-08 Ω·m | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
4.3e-08 Ω·m Show Material materials with Electrical resistivity of 4.3e-08 Ω·m | H18 | Typical value | ||
Specific Electrical conductivity | 40.0 % IACS Show Material materials with Specific Electrical conductivity of 40.0 % IACS | H18 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 96.8 - 99.0 % Show Material materials with Aluminium of 96.8 - 99.0 % | H18 | |
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 |
0.7 % Show Material materials with Iron of 0.7 % | H18 | ||
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H18 | |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H25) | |
| Workability | general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18) | |