AA Standards Grade 3004 H19

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where AA Standards Grade 3004 H19 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.72 - 2.8 g/cm³ at 20 °C

Mechanical

Elastic modulus

E

69 GPa at 20 °C

Show 3000 Series materials with Elastic modulus of 69 GPa at 20 °C

Elongation

A

1.2 % at 20 °C

Show 3000 Series materials with Elongation of 1.2 % at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 3000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 3000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 3000 Series Aluminium

Shear modulus

G

25 - 26 GPa at 20 °C

Show 3000 Series materials with Shear modulus of 25 - 26 GPa at 20 °C

Typical for Wrought 3000 Series Aluminium

Tensile strength

Rm

310 MPa at 20 °C

Show 3000 Series materials with Tensile strength of 310 MPa at 20 °C

Yield strength

YS

280 MPa at 20 °C

Show 3000 Series materials with Yield strength of 280 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.39E-5 - 2.4E-5 1/K at 20 °C

Hide chart

Melting point

Tm

630 - 655 °C

Specific heat capacity

cp

890 J/(kg·K) at 20 °C

Thermal conductivity

λ

160 - 163 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.40E+7 - 2.44E+8 S/m at 20 °C

Electrical resistivity

ρel

4.17E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Al

95.6 - 98.2 %

Mn

1 - 1.5 %

Mg

0.8 - 1.3 %

Cu

0 - 0.25 %

Fe

0 - 0.7 %

More

Technological properties

Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)

This material data has been provided by MakeItFrom.com,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.