Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | H28 | AA Standards, ASTM B209 |
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H28 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H28 | AA Standards, ASTM B209 | |
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | H28 | AA Standards, ASTM B209 | A50 |
1.7 % Show Material materials with Elongation of 1.7 % | H28 | |||
2.0 % Show Material materials with Elongation of 2.0 % | H28 | AA Standards, ASTM B209 | A50 | |
4.0 % Show Material materials with Elongation of 4.0 % | H28 | AA Standards, ASTM B209 | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 - 26.0 GPa Show Material materials with Shear modulus of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Tensile strength | 260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | H28 | AA Standards, ASTM B209 | |
300.0 MPa Show Material materials with Tensile strength of 300.0 MPa | H28 | |||
Yield strength | 215.0 MPa Show Material materials with Yield strength of 215.0 MPa | H28 | AA Standards, ASTM B209 | RP02 |
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | H28 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H28 | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H28 | AA Standards, ASTM B209 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H28 | AA Standards, ASTM B209 | |
Melting point | 630.0 - 655.0 °C Show Material materials with Melting point of 630.0 - 655.0 °C | H28 | AA Standards, ASTM B209 | |
630.0 °C Show Material materials with Melting point of 630.0 °C | H28 | |||
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | H28 | ||
Thermal conductivity | 160.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 W/(m·K) | H28 | ||
163 W/(m·K) Show Material materials with Thermal conductivity of 163 W/(m·K) | H28 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 S/m | H28 | AA Standards, ASTM B209 |
Electrical resistivity | 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 4.17e-08 Ω·m | H28 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.6 - 98.2 % Show Material materials with Aluminium of 95.6 - 98.2 % | H28 | |
Copper | 0.25 % Show Material materials with Copper of 0.25 % | H28 | AA Standards, ASTM B209 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H28 | AA Standards, ASTM B209 |
0.7 % Show Material materials with Iron of 0.7 % | H28 | ||
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | H28 | AA Standards, ASTM B209 |
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | H28 | AA Standards, ASTM B209 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H28 | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | H28 | AA Standards, ASTM B209 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H28 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |