Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | H32 | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H32 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | H32 | AA Standards | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | H32 | |||
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | H32 | AA Standards, ASTM B209 | A50 |
3.0 % Show Material materials with Elongation of 3.0 % | H32 | AA Standards, ASTM B209, ASTM B313 | A50 | |
5.0 % Show Material materials with Elongation of 5.0 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | |
5.0 % Show Material materials with Elongation of 5.0 % | H32 | AA Standards, ASTM B209 | A100 | |
6.0 % Show Material materials with Elongation of 6.0 % | H32 | AA Standards, ASTM B209, ASTM B547 | A50 | |
9.1 % Show Material materials with Elongation of 9.1 % | H32 | |||
10.0 % Show Material materials with Elongation of 10.0 % | H32 | AA Standards | A50 | |
13.5 % Show Material materials with Elongation of 13.5 % | H32 | |||
15.0 % Show Material materials with Elongation of 15.0 % | H32 | AA Standards | A100 | |
Fatigue strength | 15 MPa Show Material materials with Fatigue strength of 15 MPa | H32 | for 5x10⁸ cycles | |
Hardness, Brinell | 52.0 [-] Show Material materials with Hardness, Brinell of 52.0 [-] | H32 | AA Standards | |
52.0 [-] Show Material materials with Hardness, Brinell of 52.0 [-] | H32 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H32 | ||
Shear strength | 115.0 MPa Show Material materials with Shear strength of 115.0 MPa | H32 | ||
Tensile strength | 190.0 - 240.0 MPa Show Material materials with Tensile strength of 190.0 - 240.0 MPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | H32 | |||
215.0 MPa Show Material materials with Tensile strength of 215.0 MPa | H32 | AA Standards | ||
215 MPa Show Material materials with Tensile strength of 215 MPa | H32 | |||
Yield strength | 145.0 MPa Show Material materials with Yield strength of 145.0 MPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | RP02 |
170.0 MPa Show Material materials with Yield strength of 170.0 MPa | H32 | AA Standards | RP02 | |
170 MPa Show Material materials with Yield strength of 170 MPa | H32 | RP02 | ||
170.0 MPa Show Material materials with Yield strength of 170.0 MPa | H32 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H32 | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
Melting point | 630.0 - 655.0 °C Show Material materials with Melting point of 630.0 - 655.0 °C | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
630.0 °C Show Material materials with Melting point of 630.0 °C | H32 | |||
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | H32 | ||
Thermal conductivity | 160.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 W/(m·K) | H32 | ||
163 W/(m·K) Show Material materials with Thermal conductivity of 163 W/(m·K) | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 S/m | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Electrical resistivity | 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 4.17e-08 Ω·m | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.6 - 98.2 % Show Material materials with Aluminium of 95.6 - 98.2 % | H32 | |
Copper | 0.25 % Show Material materials with Copper of 0.25 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
0.7 % Show Material materials with Iron of 0.7 % | H32 | ||
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H32 | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |