AA Standards Grade 3004 H38

View suppliers (23)
Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.72 g/cm³

Show Material materials with Density of 2.72 g/cm³

H38

AA Standards, ASTM B209, ASTM B313

2.72 g/cm³

Show Material materials with Density of 2.72 g/cm³

H38

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

H38

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

110.0 MPa

Show Material materials with Bending Fatigue Strength of 110.0 MPa

H38

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H38

AA Standards, ASTM B209, ASTM B313

69 GPa

Show Material materials with Elastic modulus of 69 GPa

H38

Elongation

-195 °C

20 %

Show Material materials with Elongation of 20 %

H38

Elongation in 50 mm

-80 °C

10 %

Show Material materials with Elongation of 10 %

H38

Elongation in 50 mm

1.0 %

Show Material materials with Elongation of 1.0 %

H38

AA Standards, ASTM B209

A50

2.0 %

Show Material materials with Elongation of 2.0 %

H38

AA Standards, ASTM B209, ASTM B313

A50

3.8 %

Show Material materials with Elongation of 3.8 %

H38

4.0 %

Show Material materials with Elongation of 4.0 %

H38

AA Standards, ASTM B209, ASTM B313

A50

5.0 %

Show Material materials with Elongation of 5.0 %

H38

AA Standards

A50

5.0 %

Show Material materials with Elongation of 5.0 %

H38

AA Standards

A100

0 °C

7 %

Show Material materials with Elongation of 7 %

H38

Elongation in 50 mm

24 °C

6 %

Show Material materials with Elongation of 6 %

H38

Elongation in 50 mm

100 °C

7 %

Show Material materials with Elongation of 7 %

H38

Elongation in 50 mm

150 °C

15 %

Show Material materials with Elongation of 15 %

H38

Elongation in 50 mm

205 °C

30 %

Show Material materials with Elongation of 30 %

H38

Elongation in 50 mm

260 °C

50 %

Show Material materials with Elongation of 50 %

H38

Elongation in 50 mm

315 °C

80 %

Show Material materials with Elongation of 80 %

H38

Elongation in 50 mm

370 °C

90 %

Show Material materials with Elongation of 90 %

H38

Elongation in 50 mm

Fatigue strength

16 MPa

Show Material materials with Fatigue strength of 16 MPa

H38

for 5x10⁸ cycles

Hardness, Brinell

77.0 [-]

Show Material materials with Hardness, Brinell of 77.0 [-]

H38

AA Standards

77.0 [-]

Show Material materials with Hardness, Brinell of 77.0 [-]

H38

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 3000 Series Aluminium

Shear modulus

25.0 GPa

Show Material materials with Shear modulus of 25.0 GPa

H38

Shear strength

145.0 MPa

Show Material materials with Shear strength of 145.0 MPa

H38

Tensile strength

-195 °C

400 MPa

Show Material materials with Tensile strength of 400 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

303 MPa

Show Material materials with Tensile strength of 303 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260.0 MPa

Show Material materials with Tensile strength of 260.0 MPa

H38

AA Standards, ASTM B209, ASTM B313

285.0 MPa

Show Material materials with Tensile strength of 285.0 MPa

H38

AA Standards

290.0 MPa

Show Material materials with Tensile strength of 290.0 MPa

H38

0 °C

290 MPa

Show Material materials with Tensile strength of 290 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

283 MPa

Show Material materials with Tensile strength of 283 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

275 MPa

Show Material materials with Tensile strength of 275 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

215 MPa

Show Material materials with Tensile strength of 215 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

152 MPa

Show Material materials with Tensile strength of 152 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

83 MPa

Show Material materials with Tensile strength of 83 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

35 MPa

Show Material materials with Tensile strength of 35 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-200 °C

295 MPa

Show Material materials with Yield strength of 295 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-100 °C

267 MPa

Show Material materials with Yield strength of 267 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-30 °C

245 MPa

Show Material materials with Yield strength of 245 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

215.0 MPa

Show Material materials with Yield strength of 215.0 MPa

H38

AA Standards, ASTM B209, ASTM B313

RP02

250.0 MPa

Show Material materials with Yield strength of 250.0 MPa

H38

AA Standards

RP02

250.0 MPa

Show Material materials with Yield strength of 250.0 MPa

H38

25 °C

245 MPa

Show Material materials with Yield strength of 245 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

245 MPa

Show Material materials with Yield strength of 245 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

200 °C

105 MPa

Show Material materials with Yield strength of 105 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

300 °C

34 MPa

Show Material materials with Yield strength of 34 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

400 °C

19 MPa

Show Material materials with Yield strength of 19 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated Standards

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H38

20 °C

2.3899999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K

H38

AA Standards, ASTM B209, ASTM B313

100 °C

2.3899999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K

H38

AA Standards, ASTM B209, ASTM B313

Melting point

630.0 - 655.0 °C

Show Material materials with Melting point of 630.0 - 655.0 °C

H38

AA Standards, ASTM B209, ASTM B313

630.0 °C

Show Material materials with Melting point of 630.0 °C

H38

Specific heat capacity

890.0 J/(kg·K)

Show Material materials with Specific heat capacity of 890.0 J/(kg·K)

H38

Thermal conductivity

160.0 W/(m·K)

Show Material materials with Thermal conductivity of 160.0 W/(m·K)

H38

163 W/(m·K)

Show Material materials with Thermal conductivity of 163 W/(m·K)

H38

AA Standards, ASTM B209, ASTM B313

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

24000000.0 S/m

Show Material materials with Electrical conductivity of 24000000.0 S/m

H38

AA Standards, ASTM B209, ASTM B313

Electrical resistivity

4.17e-08 Ω·m

Show Material materials with Electrical resistivity of 4.17e-08 Ω·m

H38

AA Standards, ASTM B209, ASTM B313

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

95.6 - 98.2 %

Show Material materials with Aluminium of 95.6 - 98.2 %

H38

Copper

0.25 %

Show Material materials with Copper of 0.25 %

H38

AA Standards, ASTM B209, ASTM B313

Iron

0.70 %

Show Material materials with Iron of 0.70 %

H38

AA Standards, ASTM B209, ASTM B313

0.7 %

Show Material materials with Iron of 0.7 %

H38

Magnesium

0.8 - 1.3 %

Show Material materials with Magnesium of 0.8 - 1.3 %

H38

AA Standards, ASTM B209, ASTM B313

Manganese

1.0 - 1.5 %

Show Material materials with Manganese of 1.0 - 1.5 %

H38

AA Standards, ASTM B209, ASTM B313

Other

0.15 %

Show Material materials with Other of 0.15 %

H38

Silicon

0.3 %

Show Material materials with Silicon of 0.3 %

H38

AA Standards, ASTM B209, ASTM B313

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H38

AA Standards, ASTM B209, ASTM B313

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)