General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | O | AA Standards, ASTM B209 |
2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | O | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | O |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | O | AA Standards, ASTM B209 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | O | |||
Elongation | 16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B209 | A50 |
19.0 % Show Material materials with Elongation of 19.0 % | O | AA Standards, ASTM B209 | A50 | |
20.0 % Show Material materials with Elongation of 20.0 % | O | AA Standards, ASTM B209 | A50 | |
21.0 % Show Material materials with Elongation of 21.0 % | O | |||
24.0 % Show Material materials with Elongation of 24.0 % | O | AA Standards | A50 | |
24 % Show Material materials with Elongation of 24 % | O | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | O | ||
Shear strength | 83.0 MPa Show Material materials with Shear strength of 83.0 MPa | O | ||
Tensile strength | 95.0 - 145.0 MPa Show Material materials with Tensile strength of 95.0 - 145.0 MPa | O | AA Standards, ASTM B209 | |
115.0 MPa Show Material materials with Tensile strength of 115.0 MPa | O | AA Standards | ||
115 MPa Show Material materials with Tensile strength of 115 MPa | O | |||
120.0 MPa Show Material materials with Tensile strength of 120.0 MPa | O | |||
Yield strength | 35.0 MPa Show Material materials with Yield strength of 35.0 MPa | O | AA Standards, ASTM B209 | RP02 |
48.0 MPa Show Material materials with Yield strength of 48.0 MPa | O | |||
55.0 MPa Show Material materials with Yield strength of 55.0 MPa | O | AA Standards | RP02 | |
55 MPa Show Material materials with Yield strength of 55 MPa | O | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | O | ||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards, ASTM B209 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards, ASTM B209 | |
Melting point | 635.0 - 655.0 °C Show Material materials with Melting point of 635.0 - 655.0 °C | O | AA Standards, ASTM B209 | |
640.0 °C Show Material materials with Melting point of 640.0 °C | O | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | O | ||
Thermal conductivity | 170.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 W/(m·K) | O | ||
172 W/(m·K) Show Material materials with Thermal conductivity of 172 W/(m·K) | O | AA Standards, ASTM B209 |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 26000000.0 S/m Show Material materials with Electrical conductivity of 26000000.0 S/m | O | AA Standards, ASTM B209 | |
26000000 S/m Show Material materials with Electrical conductivity of 26000000 S/m | O | Typical/derived value | ||
Electrical resistivity | 3.85e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 Ω·m | O | AA Standards, ASTM B209 | |
Specific Electrical conductivity | 45.0 % IACS Show Material materials with Specific Electrical conductivity of 45.0 % IACS | O | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 96.0 - 99.5 % Show Material materials with Aluminium of 96.0 - 99.5 % | O | |
Chromium | 0.2 % Show Material materials with Chromium of 0.2 % | O | AA Standards, ASTM B209 |
Copper | 0.3 % Show Material materials with Copper of 0.3 % | O | AA Standards, ASTM B209 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | O | AA Standards, ASTM B209 |
0.7 % Show Material materials with Iron of 0.7 % | O | ||
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | O | AA Standards, ASTM B209 |
Manganese | 0.3 - 0.8 % Show Material materials with Manganese of 0.3 - 0.8 % | O | AA Standards, ASTM B209 |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | O | AA Standards, ASTM B209 |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | O | AA Standards, ASTM B209 |
Zinc | 0.4 % Show Material materials with Zinc of 0.4 % | O | AA Standards, ASTM B209 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12), poor (H14, H25, H16, H18) | |
Workability | general (condition): good (O), acceptable (H12, H14, H25), poor(H16, H18) |