Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.69 g/cm³ Show Material materials with Density of 2.69 g/cm³ | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
2.69 g/cm³ Show Material materials with Density of 2.69 g/cm³ | H32 | ||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H32 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | H32 | AA Standards | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | H32 | |||
Elongation | 4.0 % Show Material materials with Elongation of 4.0 % | H32 | AA Standards, ASTM B209 | A50 |
5.0 % Show Material materials with Elongation of 5.0 % | H32 | AA Standards, ASTM B209, ASTM B313 | A50 | |
6.0 % Show Material materials with Elongation of 6.0 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | |
6.8 % Show Material materials with Elongation of 6.8 % | H32 | |||
9.0 % Show Material materials with Elongation of 9.0 % | H32 | AA Standards | A50 | |
9 % Show Material materials with Elongation of 9 % | H32 | |||
Fatigue strength | 90 MPa Show Material materials with Fatigue strength of 90 MPa | H32 | for 5x10⁸ cycles | |
Hardness, Brinell | 46.0 [-] Show Material materials with Hardness, Brinell of 46.0 [-] | H32 | AA Standards | |
46.0 [-] Show Material materials with Hardness, Brinell of 46.0 [-] | H32 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H32 | ||
Shear strength | 115.0 MPa Show Material materials with Shear strength of 115.0 MPa | H32 | ||
Tensile strength | 150.0 - 195.0 MPa Show Material materials with Tensile strength of 150.0 - 195.0 MPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | H32 | AA Standards, ASTM B210, ASTM B483 | ||
170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | H32 | AA Standards | ||
170 MPa Show Material materials with Tensile strength of 170 MPa | H32 | |||
Yield strength | 110.0 MPa Show Material materials with Yield strength of 110.0 MPa | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | RP02 |
130.0 MPa Show Material materials with Yield strength of 130.0 MPa | H32 | |||
145.0 MPa Show Material materials with Yield strength of 145.0 MPa | H32 | AA Standards | RP02 | |
145 MPa Show Material materials with Yield strength of 145 MPa | H32 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H32 | |||
20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 625.0 - 650.0 °C Show Material materials with Melting point of 625.0 - 650.0 °C | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
630.0 °C Show Material materials with Melting point of 630.0 °C | H32 | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H32 | |||
Thermal conductivity | 190.0 W/(m·K) Show Material materials with Thermal conductivity of 190.0 W/(m·K) | H32 | |||
193 W/(m·K) Show Material materials with Thermal conductivity of 193 W/(m·K) | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 29000000.0 S/m Show Material materials with Electrical conductivity of 29000000.0 S/m | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Electrical resistivity | 3.45e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 Ω·m | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 96.3 - 98.9 % Show Material materials with Aluminium of 96.3 - 98.9 % | H32 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Copper | 0.2 % Show Material materials with Copper of 0.2 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
0.7 % Show Material materials with Iron of 0.7 % | H32 | ||
Magnesium | 1.1 - 1.8 % Show Material materials with Magnesium of 1.1 - 1.8 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H32 | |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O), poor (H32, H34), sufficient (H36, H38) | |
Workability | general (condition): good (O, H32), acceptable (H34), poor(H36, H38) |