Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | O |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | O | AA Standards | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
70 GPa Show Material materials with Elastic modulus of 70 GPa | O | ||||
Elongation | -195 °C | 46 % Show Material materials with Elongation of 46 % | O | Elongation in 50 mm | |
-80 °C | 35 % Show Material materials with Elongation of 35 % | O | Elongation in 50 mm | ||
13.0 % Show Material materials with Elongation of 13.0 % | O | AA Standards, ASTM B209 | A50 | ||
15.0 % Show Material materials with Elongation of 15.0 % | O | AA Standards, ASTM B209 | A50 | ||
16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B209 | A100 | ||
17.0 % Show Material materials with Elongation of 17.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
18.0 % Show Material materials with Elongation of 18.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
19.0 % Show Material materials with Elongation of 19.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
22.0 % Show Material materials with Elongation of 22.0 % | O | AA Standards, ASTM B211 | A100 | ||
23.0 % Show Material materials with Elongation of 23.0 % | O | ||||
25.0 % Show Material materials with Elongation of 25.0 % | O | AA Standards, ASTM B211 | A50 | ||
27.0 % Show Material materials with Elongation of 27.0 % | O | AA Standards | A100 | ||
0 °C | 32 % Show Material materials with Elongation of 32 % | O | Elongation in 50 mm | ||
24 °C | 30 % Show Material materials with Elongation of 30 % | O | Elongation in 50 mm | ||
100 °C | 36 % Show Material materials with Elongation of 36 % | O | Elongation in 50 mm | ||
150 °C | 50 % Show Material materials with Elongation of 50 % | O | Elongation in 50 mm | ||
205 °C | 60 % Show Material materials with Elongation of 60 % | O | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongation of 80 % | O | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongation of 110 % | O | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongation of 130 % | O | Elongation in 50 mm | ||
Fatigue strength | 110 MPa Show Material materials with Fatigue strength of 110 MPa | O | for 5x10⁸ cycles | ||
Hardness, Brinell | 47.0 [-] Show Material materials with Hardness, Brinell of 47.0 [-] | O | AA Standards | ||
47.0 [-] Show Material materials with Hardness, Brinell of 47.0 [-] | O | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | O | |||
Shear strength | 125.0 MPa Show Material materials with Shear strength of 125.0 MPa | O | |||
Tensile strength | -195 °C | 303 MPa Show Material materials with Tensile strength of 303 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
170.0 - 215.0 MPa Show Material materials with Tensile strength of 170.0 - 215.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
170.0 - 240.0 MPa Show Material materials with Tensile strength of 170.0 - 240.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241 | |||
170.0 - 220.0 MPa Show Material materials with Tensile strength of 170.0 - 220.0 MPa | O | AA Standards, ASTM B211 | |||
170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | O | AA Standards, ASTM B483 | |||
190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | O | ||||
0 °C | 193 MPa Show Material materials with Tensile strength of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
195.0 MPa Show Material materials with Tensile strength of 195.0 MPa | O | AA Standards | |||
220.0 MPa Show Material materials with Tensile strength of 220.0 MPa | O | AA Standards, ASTM B316 | |||
24 °C | 193 MPa Show Material materials with Tensile strength of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 193 MPa Show Material materials with Tensile strength of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 117 MPa Show Material materials with Tensile strength of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Tensile strength of 83 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Tensile strength of 35 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -196 °C | 110 MPa Show Material materials with Yield strength of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
65.0 MPa Show Material materials with Yield strength of 65.0 MPa | O | AA Standards, ASTM B209, ASTM B211, ASTM B313, ASTM B547 | RP02 | ||
70.0 MPa Show Material materials with Yield strength of 70.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B483 | RP02 | ||
80.0 MPa Show Material materials with Yield strength of 80.0 MPa | O | ||||
90.0 MPa Show Material materials with Yield strength of 90.0 MPa | O | AA Standards | RP02 | ||
24 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 76 MPa Show Material materials with Yield strength of 76 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 52 MPa Show Material materials with Yield strength of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 38 MPa Show Material materials with Yield strength of 38 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 21 MPa Show Material materials with Yield strength of 21 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | O | |||
20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C Show Material materials with Melting point of 605.0 - 650.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
610.0 °C Show Material materials with Melting point of 610.0 °C | O | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | O | |||
Thermal conductivity | 138 W/(m·K) Show Material materials with Thermal conductivity of 138 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
140.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 W/(m·K) | O |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 20000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
20300000 S/m Show Material materials with Electrical conductivity of 20300000 S/m | O | Unstated/Typical value, Typical/derived value | ||
Electrical resistivity | 5e-08 Ω·m Show Material materials with Electrical resistivity of 5e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
Specific Electrical conductivity | 35.0 % IACS Show Material materials with Specific Electrical conductivity of 35.0 % IACS | O | Unstated value, Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.8 - 97.7 % Show Material materials with Aluminium of 95.8 - 97.7 % | O | |
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
0.4 % Show Material materials with Iron of 0.4 % | O | ||
Magnesium | 2.2 - 2.8 % Show Material materials with Magnesium of 2.2 - 2.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |